Ce–Si Mixed Oxide: A High Sulfur Resistant Catalyst in the NH 3 –SCR Reaction through the Mechanism-Enhanced Process

Wei Tan,Annai Liu,Shaohua Xie,Yong Yan,Thomas E. Shaw,Yu Pu,Kai Guo,Lulu Li,Shuohan Yu,Fei Gao,Fudong Liu,Lin Dong

DOI: https://doi.org/10.1021/acs.est.0c08410

2021-03-03

Abstract:Investigating catalytic reaction mechanisms could help guide the design of catalysts. Here, aimed at improving both the catalytic performance and SO₂ resistance ability of catalysts in the selective reduction of NO by NH₃ (NH₃–SCR), an innovative CeO₂–SiO₂ mixed oxide catalyst (CeSi2) was developed based on our understanding of both the sulfur poisoning and reaction mechanisms, which exhibited excellent SO₂/H₂O resistance ability even in the harsh working conditions (containing 500 ppm of SO₂ and 5% H₂O). The strong interaction between Ce and Si (Ce–O–Si) and the abundant surface hydroxyl groups on CeSi2 not only provided fruitful surface acid sites but also significantly inhibited SO₂ adsorption. The NH₃–SCR performance of CeSi2 was promoted by an enhanced Eley–Rideal (E–R) mechanism in which more active acid sites were preserved under the reaction conditions and gaseous NO could directly react with adsorbed NH₃. This mechanism-enhanced process was even further promoted on sulfated CeSi2. This work provides a reaction mechanism-enhanced strategy to develop an environmentally friendly NH₃–SCR catalyst with superior SO₂ resistance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.0c08410?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.0c08410</a>.Information about catalytic performance tests; catalyst characterizations; texture properties; NH₃–SCR activity of recently reported catalysts in presence of SO₂ and H₂O; BET surface areas; fitting results of EXAFS oscillations for CeSi2 and CeO₂; surface atomic concentrations and Ce³⁺ ratios of CeSi2, Ce/2Si, and CeO₂; fitting results of XANES spectra of CeSi2 and CeO₂; NH₃ oxidation activity of CeSi2, Ce/2Si, and CeO₂; NH₃–SCR performance of CeSi2 and Ce/2Si cycling test; TG plots of fresh and used CeO₂, Ce/2Si, and CeSi2; SO₂-TPD profiles of CeO₂ and CeSi2; H₂-TPR profiles of fresh and used CeO₂, Ce/2Si, and CeSi2; NH₃–SCR activity of Cu-SSZ-13 and V₂O₅–WO₃/TiO₂; elemental mapping images of Ce/2Si and CeSi2; XANES spectra of Ce L₃ edge for CeO₂ and CeSi2; <i>in situ</i> DRIFTS of NH₃ adsorption–desorption on CeSi2; and NO-TPD profiles of CeO₂ and CeSi2 (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.0c08410/suppl_file/es0c08410_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

environmental sciences,engineering, environmental

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve

This paper aims to address the issue of sulfur poisoning of catalysts in the selective catalytic reduction (NH₃-SCR) reaction. Specifically, the researchers developed a CeO₂-SiO₂ mixed oxide catalyst (CeSi₂) to enhance its catalytic performance and sulfur poisoning resistance under conditions of high SO₂ concentration (500 ppm) and water vapor (5% H₂O). Through a mechanism enhancement process, this novel catalyst exhibits excellent NO removal efficiency and sulfur poisoning resistance under harsh working conditions.

### Main Research Content

1. **Design and Synthesis of the Catalyst**:
- The researchers synthesized the CeO₂-SiO₂ mixed oxide catalyst (CeSi₂) with a molar ratio of Ce to Si of 1:2 through a co-precipitation method.
- The structure and surface properties of CeSi₂ were analyzed in detail using various characterization techniques (such as XRD, Raman spectroscopy, HR-TEM, EXAFS, XPS, etc.).

2. **Performance Testing of the Catalyst**:
- The NH₃-SCR activity and N₂ selectivity of CeSi₂, Ce/2Si (CeO₂ supported on SiO₂), and pure CeO₂ were tested at different temperatures.
- The sulfur poisoning resistance and stability of the catalyst under high SO₂ and H₂O conditions were evaluated through cyclic activity tests and long-term stability tests.

3. **Study of the Reaction Mechanism**:
- The NH₃-SCR reaction mechanism on CeSi₂ was revealed through in-situ DRIFTS experiments, showing that it mainly follows the Eley-Rideal (E-R) mechanism.
- After sulfation treatment, CeSi₂ still maintained an efficient E-R mechanism, further enhancing its sulfur poisoning resistance.

### Main Conclusions

- **Structural Characteristics**:
- CeSi₂ forms a unique Ce-O-Si structure and has a surface rich in hydroxyl groups. These characteristics not only provide more surface acidic sites but also significantly inhibit SO₂ adsorption.

- **Catalytic Performance**:
- CeSi₂ exhibits excellent NH₃-SCR activity and sulfur poisoning resistance under high SO₂ and H₂O conditions, outperforming widely used commercial catalysts (such as Cu-SSZ-13 and V₂O₅-WO₃/TiO₂) and some recently reported novel catalysts.

- **Reaction Mechanism**:
- CeSi₂ effectively promotes the direct reaction of active NH₃ with gaseous NO through an enhanced E-R mechanism, reducing the competitive adsorption of inert nitrate species, thereby improving catalytic performance and sulfur poisoning resistance.

### Significance

This work provides a new strategy for designing efficient NH₃-SCR catalysts with high sulfur poisoning resistance. By understanding and utilizing various mechanistic pathways in the NH₃-SCR process, more environmentally friendly catalysts can be developed for treating exhaust emissions containing high concentrations of SO₂.