Depth investigation of the regulation mechanism of SiO 2 on the denitrification performance and sulfur resistance of MnCe/Ti SCR catalyst
Mengxia Qing,Linlin Zhang,Liang Liu,Yaxin Chen,Yunda Su,Sheng Su,Song Hu,Yi Wang,Jun Xiang
DOI: https://doi.org/10.1016/j.cej.2023.145852
IF: 15.1
2023-09-23
Chemical Engineering Journal
Abstract:The "deep peaking" of coal-fired units presents great challenges for SCR catalysts' de-NO x activity at wide temperatures. Mn-based catalysts have good de-NO x activity at low temperatures, but their poor sulfur resistance is one of the key issues affecting industrial applications. In this study, the effects of SiO 2 doping on the denitrification, sulfur resistance, and physicochemical performance of the MnCe/Ti catalyst were investigated. The results showed that SiO 2 improved the de-NO x activity of catalysts at high temperatures and enhanced SO 2 /H 2 O resistance at wide temperatures. Under short reaction time conditions, the MnCe/Ti 0.9 Si 0.1 catalyst exhibited the highest NO conversion rate at 400 °C, which was 33% higher than that of the MnCe/Ti catalyst. The NO conversion rates of Si-doped MnCe/Ti catalysts increased rapidly to over 85% (65% of the MnCe/Ti catalyst) as the reaction temperature increased from 200 °C to 250 °C under SO 2 -containing atmosphere due to the promoting effects of SiO 2 on the decomposition of ammonium bisulfate. MnCe/Ti 0.7 Si 0.3 catalyst exhibited the optimal sulfur and H 2 O resistance, with NO conversion rate higher than 85% with 600 min under SO 2 /H 2 O-containing atmospheres. SiO 2 inhibited the crystallization of anatase TiO 2 , and increased the specific surface area to 306.60 m 2 /g. Additionally, the ratios of Mn 4+ /Mn n+ and Ce 3+ /Ce m+ , and the surface adsorbed oxygen and weak-medium acid amount also increased due to the multiple interactions between the TiO 2 -SiO 2 and Mn/Ce, resulting in the higher de-NO x activity. Compared with the MnCe/Ti catalyst, Si-doped MnCe/Ti catalysts have lower SO 2(g) adsorption amount and the sulfation of Mn, and higher SO 3(a) desorption performance, resulting in better sulfur resistance at wide temperatures.
engineering, chemical, environmental