Laser powder bed fusion of Mo2C/Ti-6Al-4V composites with alternately laminated α′/β phases for enhanced mechanical properties

Chao Cai,Jasper Chua Dong Qiu,Tey Wei Shian,Changjun Han,Tong Liu,Ling Bing Kong,Narasimalu Srikanth,Chen-Nan Sun,Kun Zhou

DOI: https://doi.org/10.1016/j.addma.2021.102134

IF: 11

2021-10-01

Additive Manufacturing

Abstract:<p>Mo₂C/Ti64 composites with nearly full densification and enhanced tensile strength were developed by using laser powder bed fusion (LPBF). The addition of 1–3 wt.% Mo₂C particles with an average particle size of ~1 μm enabled the LPBF-printed composites with an alternately laminated α′-Ti/β-Ti microstructure along with Mo₂C and <em>in-situ</em> synthesized M₂₃C₆ (M was Ti, Al, V, and Mo). During LPBF, most of the Mo₂C particles were incorporated into the Ti64 matrix, resulting in the α′-Ti and β-Ti solid solutions. The segregation of Mo contributed to the generation of the β-Ti phase at the melt pool boundaries of the composites, leading to the alternating hard α′-Ti/soft β-Ti phases. Remarkable improvements of 22.8% and 19.5% in the hardness and tensile strength of the Ti64 matrix were achieved, respectively. The strengthening of the LPBF-printed composites was associated with the formation of the laminated α′-Ti/β-Ti structure, solid solution behavior of Mo and C, and presence of the remaining Mo₂C and precipitated M₂₃C₆. The findings are anticipated to provide insights into the selection of reinforcement materials for additively manufactured composites with nearly full densities and greater mechanical strength.</p>

engineering, manufacturing,materials science, multidisciplinary