Microstructure and tensile properties of TiCp/Ti6Al4V composites by laser melting deposition with different dissolving degrees of TiC

Jiandong Wang,Yuzhou Zeng,Weihang Fan,Liqun Li,Yunxiang Tong,Zhenqiang Wang,Fengchun Jiang

DOI: https://doi.org/10.1016/j.ceramint.2022.08.052

IF: 5.532

2022-12-01

Ceramics International

Abstract:20 vol% TiCp/Ti6Al4V composites were manufactured by laser melting deposition (LMD). The tensile strength of the composites was improved by regulating dissolving degrees of TiC particles. This process was achieved through altering laser power P and defocus Δf. When P was raised from 300W to 500W, higher heat input facilitated the dissolution of TiC particles and induced the formation of more in-situ TiC phases. The TiC particles were further dissolved when elevating Δf from +3 mm to +5 mm and making powder flows focus above the substrate surface. This was because powders were pre-heated by the laser beam before entering into the molten pool. The pre-heating process further enhanced dissolving degrees of undissolved TiC particles and promoted the formation of in-situ TiC phases. The tensile strength of the composites increased from 794.0 MPa to 1091.7 MPa with dissolving degrees of TiC increasing. The strengthening mechanism was that in-situ TiC phases were less easy to crack than undissolved TiC particles.

materials science, ceramics