Abstract:An effective design strategy for preparing highly transparent polyimide film with low dielectric constant is presented. The key to the strategy is to simultaneously introduce meta-substituted structure and trifluoromethyl in polymer chains. By using this design strategy, a highly transparent polyimide film with low-k was synthesized from 3,5-diaminobenzotrifluoride (m-TFPDA) and 4,4′-(hexafluoroisopropylidene) diphthalic anhydride (6FDA) through a two-step method. The obtained m-TFPDA/6FDA (CPI) film (∼30 µm) possesses high optical transparency (λcutoff=334 nm, T450nm=85.26%, Haze=0.31) and is close to colorless (L*=96.03, a*=−0.34, b*=2.12, yellow index=3.96). The intrinsic k and dielectric loss value of the film are 2.27 and 0.0013 at 10 kHz, respectively. More importantly, such low dielectric performance could remain stable up to 280 °C, and the film shows a low moisture rate (∼0.51%), which helps to maintain the low-k property stability in different humid environments. Meanwhile, the film also shows good thermal stability and mechanical properties, with a glass transition temperature (Tg) of 296 °C and the 5 wt% decomposition temperature (Td,5%) of 522 °C under N2. The tensile strength and tensile modulus of the film are 85.1 MPa and 1.96 GPa, respectively. In addition, the film is soluble in common solvents, which allows simple solution processing and low-cost, continuous roll-to-roll processes. This design strategy is beneficial to improving the transparency, lightening yellow color, lowering the dielectric constant and meanwhile maintaining the comprehensive properties of polyimide films, which is mainly due to the introduced meta-substituted and trifluoromethyl structures effectively inhibiting the transfer of charge transfer complex (CTC) effects and increasing the free volume of film. This design strategy could also be extended to other high-performance polymer systems.

Polyimide Films with Liquid‐Crystal‐Like Structures: Toward Ultralow Dielectric Loss at High Frequencies

Polyimide Foams with Ultralow Dielectric Constants

Polyimide films with ultralow dielectric loss for 5G applications: Influence and mechanism of ester groups in molecular chains

Poly(ester imide)s with Low Linear Coefficients of Thermal Expansion and Low Water Uptake (VII): A Strategy to Achieve Ultra-Low Dissipation Factors at 10 GHz

Emerging ionic liquid-induced porous polyimide films toward ultralow permittivity, improved hydrophobic and electromagnetic wave absorption

Preparation of fluorinated polyimides with low dielectric constants and low dielectric losses by combining ester groups and triphenyl pyridine structures

Ultra-low-permittivity, high hydrophobic, and excellent thermally stable fluoroelastomer/polyimide composite films employing dielectric reduction

Polyimide/crown ether composite film with low dielectric constant and low dielectric loss for high signal transmission

Systematically studied the relationship between high-frequency dielectric dissipation factor and water adsorption of polyimide film

Low—Permittivity Copolymerized Polyimides with Fluorene Rigid Conjugated Structure

Fluorinated polyimide with triphenyl pyridine structure for 5G communications: Low dielectric, highly hydrophobic, and highly transparent

Synthesis and Characterization of High Fluorine‐containing Polyimides with Low‐dielectric Constant

Preparation of Polyimide Films with Ultra-Low Dielectric Constant by Phase Inversion

Construction of fluorenyl‐modified low dielectric constant polyimide films with excellent mechanical properties and optical transparency

Porous polyimide composite films containing mesoporous hollow silica nanospheres with ultralow dielectric constant and dissipation loss

Perfluorocyclobutyl-containing transparent polyimides with low dielectric constant and low dielectric loss

Crown Ether Copolymerized Polyimide Film: Enhanced Mechanical, Thermal Properties and Low Dielectric Constant under High Frequency

Synthesis and applications of low dielectric polyimide

Highly Transparent and Colorless Polyimide Film with Low Dielectric Constant by Introducing Meta-substituted Structure and Trifluoromethyl Groups

Thermoplastic Polyimide with Low Dielectric Properties Enabled by the 2,2′-Spirobifluorene Group

Mechanically Strong, Transparent Polyimide Composite Thin Films with a Low Dielectric Constant