Composite anti-scaling membrane made of interpenetrating networks of nanofibers for selective separation of lithium

Yan Zhao,Mengyao Wu,Pengxin Shen,Collin Uytterhoeven,Natalie Mamrol,Jiangnan Shen,Congjie Gao,Bart Van der Bruggen

DOI: https://doi.org/10.1016/j.memsci.2020.118668

IF: 9.5

2021-01-01

Journal of Membrane Science

Abstract:<p>The selective separation and extraction of lithium from salt lakes is compromised by the high salt concentration and the presence of competing ions. In this study, a class of novel cation exchange membranes based on Kevlar aramid nanofibers (KANFs) was designed via interpenetrating networks of poly(4-styrenesulfonic acid-co-maleic acid) sodium salt (PSSMA) and amide reaction of 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (ATTO). Membranes with different PSSMA content were fabricated, and the final membrane denoted as A# achieved a ∼1.2 mmol g⁻¹ ion exchange capacity, ∼28% water content, ∼4.5% swelling rate and ∼1.8 Ω cm² surface electrical resistance. The thin A# membrane (∼8 μm thickness) also exhibited a high membrane limiting current density of 32.0 mA cm⁻² (in 0.1 M NaCl solution) and an exceptional desalination efficiency (99.9% for NaCl) in electrodialysis. Moreover, compared to some commercial monovalent selectivity cation exchange membranes (CSO and CIMS membranes, which are two commercial monovalent cation selective membranes), the A# membrane was found functional for the separation of Li⁺/Mg²⁺ and to have an excellent anti-scaling performance. As the selectivity has potential to be as high or higher as that of commercial membranes, this work provides a promising method to develop membranes with anti-scaling performance for the extraction of lithium from high salt concentrations in salt lakes.</p>

engineering, chemical,polymer science