Abstract:BACKGROUND:Currently, the effect of the bacterial community on cast iron corrosion process does not reach consensus. Moreover, some studies have produced contrasting results, suggesting that bacteria can either accelerate or inhibit corrosion.RESULTS:The long-term effects of the bacterial community on cast iron corrosion in reclaimed wastewater distribution systems were investigated from both spatial (yellow layer vs. black layer) and temporal (1-year dynamic process) dimensions of the iron coupon-reclaimed wastewater microcosm using high-throughput sequencing and flow cytometry approaches. Cast iron coupons in the NONdisinfection and UVdisinfection reactors suffered more severe corrosion than did those in the NaClOdisinfection reactor. The bacterial community significantly promoted cast iron corrosion, which was quantified for the first time in the practical reclaimed wastewater and found to account for at least 30.5% ± 9.7% of the total weight loss. The partition of yellow and black layers of cast iron corrosion provided more accurate information on morphology and crystal structures for corrosion scales. The black layer was dense, and the particles looked fusiform, while the yellow layer was loose, and the particles were ellipse or spherical. Goethite was the predominant crystalline phase in black layers, while corrosion products mainly existed as an amorphous phase in yellow layers. The bacterial community compositions of black layers were distinctly separated from yellow layers regardless of disinfection methods. The NONdisinfection and UVdisinfection reactors had a more similar microbial composition and variation tendency for the same layer type than did the NaClOdisinfection reactor. Biofilm development can be divided into the initial start-up stage, mid-term development stage, and terminal stable stage. In total, 12 potential functional genera were selected to establish a cycle model for Fe, N, and S metabolism. Desulfovibrio was considered to accelerate the transfer of Fe0 to Fe2+ and speed up weight loss.CONCLUSION:The long-term effect of disinfection processes on corrosion behaviors of cast iron in reclaimed wastewater distribution systems and the hidden mechanisms were deciphered for the first time. This study established a cycle model for Fe, N, and S metabolism that involved 12 functional genera and discovered the significant contribution of Desulfovibrio in promoting corrosion.

Synergistic effects of sodium hypochlorite disinfection and iron-oxidizing bacteria on early corrosion in cast iron pipes

Effect of water supply pipe wall corrosion on chlorine decay

Effects of Major Anions on Iron Release in Drinking Water Supply System

Influence Factors of Initial Internal Corrosion of Grey Cast Iron Pipes in Water Distribution System

Effects of Chloride and Humic Acid on Iron Release in Water Distribution System

Influence of microbial community on iron release under stagnation condition in drinking water systems

Effects of Disinfectant and Biofilm on the Corrosion of Cast Iron Pipes in a Reclaimed Water Distribution System

Effects of cast iron pipe corrosion on nitrogenous disinfection by-products formation in drinking water distribution systems via interaction among iron particles, biofilms, and chlorine

Early Period Corrosion and Scaling Characteristics of Ductile Iron Pipe for Ground Water Supply with Sodium Hypochlorite Disinfection.

Use of Oxidation-Reduction Potential to Monitor Iron Release from Corroded Iron Pipes in Drinking Water Distribution System

Controlling iron release of desalinated seawater transmitted in existing grey cast iron pipe

Characterization of Biofilm and Corrosion of Cast Iron Pipes in Drinking Water Distribution System with UV/Cl2 Disinfection.

Synergistic effects of trace sulfadiazine and corrosion scales on disinfection by-product formation in bulk water of cast iron pipe

Impacts of Water Quality on the Corrosion of Cast Iron Pipes for Water Distribution and Proposed Source Water Switch Strategy.

Effect of NaClO Addition on Bacteriostasis of Iron Bacteria and Corrosion Control of Pipe Line Steel for Water Distribution Network in Urban Reclaimed Water

Effects of Chlorination/chlorine Dioxide Disinfection on Biofilm Bacterial Community and Corrosion Process in a Reclaimed Water Distribution System.

[Growth Characteristics and Control of Iron Bacteria on Cast Iron in Drinking Water Distribution Systems].

Comprehensive comparison of water quality risk and microbial ecology between new and old cast iron pipe distribution systems

Effect of chloride ions on the corrosion behavior of carbon steel in an iron bacteria system

The Bacterial Community Significantly Promotes Cast Iron Corrosion in Reclaimed Wastewater Distribution Systems.

[Effect of Biofilm on the Corrosion and Fouling of Cast Iron Pipe for Water Supply].