Abstract:The long-term stagnation in metal water supply pipes, usually caused by intermittent consumption patterns, will cause significant iron release and water quality deterioration, especially at the terminus of pipelines. Another common phenomenon at the terminus of pipelines is leakage, which is considered helpful by allowing seepage of low-quality drinking water resulting from long-term stagnation. In this study, the effect of laminar flow on alleviating water quality deterioration under different leakage conditions was investigated, and the potential thresholds of the flow rate, which can affect the iron release process, were discussed. Based on a galvanized pipe and ductile cast iron pipe pilot platform, which was established at the terminus of pipelines, this research was carried out by setting a series of leakage rate gradients to analyze the influence of different leakage flow rates on iron release, as well as the relationship with chemical and biological parameters. The results showed that the water quality parameters were obviously influenced by the change in flow velocity. Water quality was gradually improved with an increase in flow velocity, but its change regularity reflected a diversity under different flow rates (p < 0.05). The iron release was remarkably correlated to the redox potential, dissolved oxygen, pH, iron-oxidized bacteria and sulfate-reducing bacteria. The cumulative total iron release (r = 0.587, p < 0.05) and total iron release rate (r = 0.71, p < 0.022) were significantly influenced by the changes in flow velocity. In short, they tended first to increase and then to decrease with an increasing flow velocity with the threshold as approximately 40% of the critical laminar flow velocity (1.16 × 10−3 m/s). For the pipes at the terminus of the drinking water distribution system, when the bulk water was at the critical laminar flow velocity, the concentration of total iron, the quantity and rate of total iron release remain relatively in an ideal and safe situation.

Early Period Corrosion and Scaling Characteristics of Ductile Iron Pipe for Ground Water Supply with Sodium Hypochlorite Disinfection.

Influence Factors of Initial Internal Corrosion of Grey Cast Iron Pipes in Water Distribution System

Effect of water supply pipe wall corrosion on chlorine decay

Effects of Chloride and Humic Acid on Iron Release in Water Distribution System

Effects of Major Anions on Iron Release in Drinking Water Supply System

Chlorination of Enoxacin (ENO) in the Drinking Water Distribution System: Degradation, Byproducts, and Toxicity.

Use of Oxidation-Reduction Potential to Monitor Iron Release from Corroded Iron Pipes in Drinking Water Distribution System

Sulfadiazine Destruction by Chlorination in a Pilot-Scale Water Distribution System: Kinetics, Pathway, and Bacterial Community Structure.

Controlling iron release of desalinated seawater transmitted in existing grey cast iron pipe

Synergistic effects of sodium hypochlorite disinfection and iron-oxidizing bacteria on early corrosion in cast iron pipes

Change regularity of water quality parameters in leakage flow conditions and their relationship with iron release.

Study on Iron Release with Various Blending of Desalinated Water and Tap Water

Manganese Release from Corrosion Products of Cast Iron Pipes in Drinking Water Distribution Systems: Effect of Water Temperature, Ph, Alkalinity, SO42- Concentration and Disinfectants

Physico-chemical Characteristics of Corrosion Scales from Different Pipes in Drinking Water Distribution Systems

Study on Electrochemical Reduction Mechanisms of Iron Oxides in Pipe Scale in Drinking Water Distribution System.

Characteristics of Iron Corrosion Scales and Water Quality Variations in Drinking Water Distribution Systems of Different Pipe Materials.

Impacts of Water Quality on the Corrosion of Cast Iron Pipes for Water Distribution and Proposed Source Water Switch Strategy.

Effect of Chloramine Residual on Iron Release in Drinking Water Distribution Systems

Review on corrosion and corrosion scale formation upon unlined cast iron pipes in drinking water distribution systems

Effects of Disinfectant and Biofilm on the Corrosion of Cast Iron Pipes in a Reclaimed Water Distribution System

Effects of chloride on corrosion scale compositions and heavy metal release in drinking water distribution systems