Abstract:Fabrication of spherical lignin nanoparticles (LNPs) is opening more application opportunities for lignin. However, dissolution of LNPs at a strongly alkaline pH or in common organic solvent systems has prevented their surface functionalization in a dispersion state as well as processing and applications that require maintaining the particle morphology under harsh conditions. Here, we report a simple method to stabilize LNPs through intraparticle cross-linking. Bisphenol A diglycidyl ether (BADGE), a cross-linker that, like lignin, contains substituted benzene rings, is coprecipitated with softwood Kraft lignin to form hybrid LNPs (hy-LNPs). The hy-LNPs with a BADGE content ≤20 wt % could be intraparticle cross-linked in the dispersion state without altering their colloidal stability. Atomic force microscopy and quartz crystal microbalance with dissipation monitoring were used to show that the internally cross-linked particles were resistant to dissolution under strongly alkaline conditions and in acetone-water binary solvent that dissolved unmodified LNPs entirely. We further demonstrated covalent surface functionalization of the internally cross-linked particles at pH 12 through an epoxy ring-opening reaction to obtain particles with pH-switchable surface charge. Moreover, the hy-LNPs with BADGE content ≥30% allowed both inter- and intraparticle cross-linking at >150 °C, which enabled their application as waterborne wood adhesives with competitive dry/wet adhesive strength (5.4/3.5 MPa).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c09500?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c09500</a>.Table showing the preparation parameters, final obtained concentrations, and yields of the hy-LNPs and LNPs; volume-based hydrodynamic diameter distributions and ζ potential distributions of the hy-LNPs and LNPs; colloidal stability of the hy-LNPs in aqueous media at various temperatures; vuring of hy-LNPs10 in dispersion state and their resistance to acetone-water (3:1, w/w) after curing; table showing the average particle heights of 0.5–8 h cured hy-LNPs20, before and after rinsing with acetone-water (3:1, w/w); IR absorption of 0 to 8 h cured hy-LNPs20; Dh and ζ potential of the uncured and 4 h cured hy-LNPs20; DLS results of the uncured hy-LNPs20 at pH 12.9; scanning electron microscopic images of the veneer surfaces with and without cured hy-LNPs30; photo showing the wood failure occurring to the 0.8 mm-thick veneers during adhesive strength test; DSC results of the hy-LNPs, mechanically blended SKL and BADGE mixture, BADGE (in solid form) and SKL; AFM and ATR-FTIR results of the hy-LNPs and LNPs after various heat-treatments; 31P NMR and XPS results of the untreated and heat-treated LNPs; SKL molar mass distribution determined with GPC (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c09500/suppl_file/nn0c09500_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Using phenol-enriched hydroxy lignin obtained by low-cost catalysts to synthesize industrial adhesive

Lignin Oligomers from Mild Base-catalyzed Depolymerization for Potential Application in Aqueous Soy Adhesive as Phenolic Blends

High-performance adhesives modified by demethylated lignin for extreme environment

Pretreatment of kraft lignin by deep eutectic solvent and its utilization in preparation of lignin-based phenolic formaldehyde adhesive

Custom-designed polyphenol lignin for the enhancement of poly(vinyl alcohol)-based wood adhesive

A Review on Lignin‐Based Phenolic Resin Adhesive

Preparation and properties of adhesives based on phenolic resin containing lignin micro and nanoparticles: A comparative study

Phenolation to Improve Hardwood Kraft Lignin for Wood Adhesive Application

Preparation and evaluation of lignin-phenol-formaldehyde resin as wood adhesive using unmodified lignin

Synthesis and characterization of a bio-aldehyde-based lignin adhesive with desirable water resistance

Performance of soybean protein adhesive cross-linked by lignin and cuprum

Broad-spectrum lignin-based adhesives using thiol–silyl ether crosslinkers

Lignin Phenol Formaldehyde Resoles Using Base-Catalysed Depolymerized Kraft Lignin

Preparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained from Bio-ethanol Production Residue

Fast Curing Bio-Based Phenolic Resins via Lignin Demethylated under Mild Reaction Condition

Characterization and properties of phenolic resin doped modified lignin

Solvent-Resistant Lignin-Epoxy Hybrid Nanoparticles for Covalent Surface Modification and High-Strength Particulate Adhesives

Lignin-Glyoxal: A Fully Biobased Formaldehyde-Free Wood Adhesive for Interior Engineered Wood Products

Preparation, optimisation and characterisation of lignin phenol formaldehyde resin as wood adhesive

Bonding wood with uncondensed lignins as adhesives