Abstract:In this study, a biobased phenolic adhesive was successfully developed by entirely substituting both petroleum-based phenol and formaldehyde with an unmodified corn stover biorefinery lignin and glyoxal (a biobased dialdehyde), respectively. Lignin-glyoxal resins were synthesized using an alkaline catalyst with a molar ratio of lignin to glyoxal of 1:2. Chemical, thermal, and mechanical properties of the lignin, lignin-based resins, and final adhesives were assessed following appropriate standard test methods. The analysis of lignins and lignin-based resin molar mass was performed using gel permeation chromatography. The lignin-glyoxal resin was found to have a 3-fold higher average molecular weight than the starting lignin, demonstrating the successful integration of lignin into the polymeric resin network. The curing of the formulated adhesives was studied using differential scanning calorimetry and dynamic mechanical analysis. Although the lignin-glyoxal resin had a higher curing temperature (167 °C) than a conventional phenol-formaldehyde resin (142 °C) and the formulated lignin-formaldehyde resin (146 °C), the rate and degree of cure were similar or better than the other two resins. The adhesion strengths of the formulated adhesives were determined using single-lap-joint veneer samples cured according to recommended press parameters for commercial adhesives. The lignin-glyoxal adhesive had a relatively high dry adhesion strength (3.9 MPa), with over 90% wood failure, but failed the wet adhesion test (boiling water test). Although the formulated lignin-glyoxal adhesive failed the boiling water test, it had excellent stability at room temperature water, remaining intact after 1 week during the water immersion test. The high dry adhesion strength makes this class of lignin-based formaldehyde-free adhesives a unique biobased glue for the production of interior grade plywood and oriented strand boards.A biobased adhesive was formulated by entirely replacing petroleum-based phenol and formaldehyde with lignin and glyoxal for interior plywood application.This article has not yet been cited by other publications.

Broad-spectrum lignin-based adhesives using thiol–silyl ether crosslinkers

A Novel Method of Self-Cross-Linking of Syringaldehyde with Activated Methoxy Groups via Cross-Coupling for Lignin-Based Wood Adhesives

Versatile value-added application of hyperbranched lignin derivatives: Water-resistance adhesive, UV protection coating, self-healing and skin-adhesive sensing

Fabrication of well-defined lignin-derived elastomers by atom transfer radical polymerization and Diels-Alder reaction towards sustainable, super-tough and high temperature-resistant hot-melt adhesives

Bioinspired 'phenol-amine' cross-linking and mineral reinforcement enable strong, tough, and formaldehyde-free tannic acid-based adhesives

High-performance adhesives modified by demethylated lignin for extreme environment

Functionalization of cellulose with amine group and cross-linked with branched epoxy to construct high-performance wood adhesive

Preparation of a Lignin-Based Vitrimer Material and Its Potential Use for Recoverable Adhesives

Lignin-Glyoxal: A Fully Biobased Formaldehyde-Free Wood Adhesive for Interior Engineered Wood Products

Performance of soybean protein adhesive cross-linked by lignin and cuprum

Lignin Oligomers from Mild Base-catalyzed Depolymerization for Potential Application in Aqueous Soy Adhesive as Phenolic Blends

Synthesis and characterization of a bio-aldehyde-based lignin adhesive with desirable water resistance

Construction of xylan-based wood adhesive via tailoring crosslinking and interfacial chemical covalent bonding

A Review on Lignin‐Based Phenolic Resin Adhesive

Using phenol-enriched hydroxy lignin obtained by low-cost catalysts to synthesize industrial adhesive

Preparation and properties of adhesives based on phenolic resin containing lignin micro and nanoparticles: A comparative study

Enzymatic Conversion of Lignosulfonate into Wood Adhesives: A Next Step towards Fully Biobased Composite Materials

Fabrication of lignin based renewable dynamic networks and its applications as self-healing, antifungal and conductive adhesives

Novel hyperbranched resin for wood adhesive: Based on air oxidation and crosslinking copolymerization strategy

Carboxymethylated Lignin Reinforcement of SPI Adhesive: Enhancing Strength, Antimicrobial, and Flame-Retardant Properties without Excessive Alkali Introduction

Custom-designed polyphenol lignin for the enhancement of poly(vinyl alcohol)-based wood adhesive