Carboxymethylated Lignin Reinforcement of SPI Adhesive: Enhancing Strength, Antimicrobial, and Flame-Retardant Properties without Excessive Alkali Introduction

Changjiang Sun,Fengxiang Cao,Yecheng Xu,Jiao Feng,Keyan Wang,Zhen Fang,Yangbing Wen

DOI: https://doi.org/10.1021/acsomega.4c00452

IF: 4.1

2024-06-03

ACS Omega

Abstract:To address the challenges associated with formaldehyde emissions in engineered wood adhesives and simultaneously enhance adhesive properties related to water resistance, fire resistance, and mold resistance, a novel environmentally sustainable biomass-based adhesive was formulated. In this work, kraft lignin was carboxymethylated and then blended with the soy protein isolate (SPI)-based adhesive, the dry and wet shear strength of the plywood bonded by the resultant adhesive was enhanced from...

chemistry, multidisciplinary

What problem does this paper attempt to address?

This paper aims to solve the formaldehyde emission problem existing in engineered wood adhesives and at the same time enhance the performance of the adhesives, especially improve their water - resistance, fire - resistance and anti - mildew properties. The research team achieved this goal by developing a new type of environmentally sustainable biomass - based adhesive. Specifically, they carboxymethylated alkali lignin (generating carboxymethylated lignin, abbreviated as CML), and then mixed it with soy protein isolate (SPI) - based adhesive to improve the dry - and - wet shear strength, anti - mildew property and fire - resistance performance of the adhesive and reduce the water absorption rate.

### Main improvement points:
1. **Improve shear strength**: By adding CML, the dry - and - wet shear strengths of the adhesive increased from 1.10 MPa and 0.63 MPa to 1.73 MPa and 1.23 MPa respectively, with an increase of 157% and 195% respectively.
2. **Enhance anti - mildew performance**: CML significantly improved the anti - mildew performance of the adhesive, making it less likely to mildew in a high - humidity environment.
3. **Improve fire - resistance performance**: CML increased the carbon content in the adhesive and provided good flame - retardant performance.
4. **Reduce water absorption rate**: The addition of CML reduced the water absorption rate of the adhesive from 190% to 108%.

### Experimental methods:
- **Material preparation**: Materials such as soy protein isolate (SPI), alkali lignin and carboxymethylated lignin (CML) were used.
- **Preparation of CML**: Alkali lignin was dissolved in sodium hydroxide solution, sodium chloroacetate was added and then the reaction was carried out by heating. Finally, CML was obtained through acidification, washing and drying.
- **Preparation of adhesive**: CML or alkali lignin was mixed with SPI, the pH value was adjusted and then a cross - linking agent was added. The adhesive was prepared by stirring evenly.
- **Performance test**: The performance of the adhesive was evaluated by methods such as dry - and - wet shear strength test, thermogravimetric analysis, FTIR and NMR spectral analysis.

### Conclusion:
By introducing carboxymethylated lignin (CML), the research team successfully developed a high - performance, high - strength, fire - resistant and anti - mildew biomass - based adhesive. Compared with commercial urea - formaldehyde adhesives and soy protein - based adhesives, this new type of adhesive performs excellently in multiple performance indicators and has broad application prospects, especially in fields such as fire - proof doors.