Self-protecting CoFeAl-layered double hydroxides enable stable and efficient brine oxidation at 2 A cm −2

Wei Liu,Jiage Yu,Tianshui Li,Shihang Li,Boyu Ding,Xinlong Guo,Aiqing Cao,Qihao Sha,Daojin Zhou,Yun Kuang,Xiaoming Sun
DOI: https://doi.org/10.1038/s41467-024-49195-z
IF: 16.6
2024-06-04
Nature Communications
Abstract:Low-energy consumption seawater electrolysis at high current density is an effective way for hydrogen production, however the continuous feeding of seawater may result in the accumulation of Cl − , leading to severe anode poisoning and corrosion, thereby compromising the activity and stability. Herein, CoFeAl layered double hydroxide anodes with excellent oxygen evolution reaction activity are synthesized and delivered stable catalytic performance for 350 hours at 2 A cm −2 in the presence of 6-fold concentrated seawater. Comprehensive analysis reveals that the Al 3+ ions in electrode are etched off by OH − during oxygen evolution reaction process, resulting in M 3+ vacancies that boost oxygen evolution reaction activity. Additionally, the self-originated Al(OH) n − is found to adsorb on the anode surface to improve stability. An electrode assembly based on a micropore membrane and CoFeAl layered double hydroxide electrodes operates continuously for 500 hours at 1 A cm −2 , demonstrating their feasibility in brine electrolysis.
multidisciplinary sciences
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the corrosion and performance degradation of the anode during seawater electrolysis under high current density. Specifically, the paper focuses on the anode poisoning and corrosion phenomena caused by Cl\(^-\) accumulation during seawater electrolysis in high - concentration salt water, which will seriously affect the activity and stability of the anode. To solve this problem, the research team has developed an anode material based on CoFeAl - layered double hydroxide (CoFeAl - LDH). This material can operate stably for more than 350 hours at a current density of 2 A cm\(^{-2}\) in 6 - times - concentrated seawater, showing excellent corrosion resistance and electrocatalytic performance. The main contribution of the paper lies in proposing a new mechanism to enhance the activity of CoFeAl - LDH through Al\(^{3+}\) vacancies generated by OH\(^-\) etching during the OER process, and the formed Al(OH)\(_n^-\) species can be partially adsorbed on the electrode surface to protect the electrode from corrosion. These findings are of great significance for promoting the practical application of seawater electrolysis technology, especially for industrial - scale applications.