Abstract:In this work, carbonate intercalation and etching‐hydrolysis strategies at room temperature and atmospheric pressure are deployed to synthesize the large‐scale and ultra‐stable electrodes for seawater splitting. The as obtained material (NiFe LDH_CO32−) exhibits impressive OER activity under alkaline simulated seawater, showing stable operation for 1000 h at 500 and 1000 mA cm−2. Owing to the presence of a substantial concentration of chlorine in seawater, the anode still faces severe chlorine corrosion, especially the water splitting operated at high current densities. Herein, the cost‐effective and scalable NiFe layered double hydroxides with carbonate intercalation (named as NiFe LDH_CO32−) are synthesized utilizing the etching‐hydrolysis and ion exchange strategies under ambient conditions. Experimental findings demonstrate that NiFe LDH_CO32− shows excellent stability at 500 and 1000 mA cm−2 for 1000 h under alkaline simulated seawater. Additionally, a two‐electrode system offers great stability at current densities ranging from 100 to 1000 mA cm−2 over a duration of 400 h in alkaline seawater. This remarkably catalytic stability can be ascribed to the etching‐hydrolysis and carbonate intercalation strategies. The etching‐hydrolysis strategy leads to an integrated electrode for the catalyst‐carrier, enhancing the adhesion between them, and retarding hence the divorce of catalysts from the carrier. Theoretical calculations suggest that the carbonate intercalation weakens the adsorbability of chlorine on catalysts and hinders the coupling of metal atoms with chlorine, thereby impeding the anode corrosion caused by chlorine and improving catalytic stability. More importantly, this strategy has been extended to the preparation of other layered double hydroxides with carbonate intercalation.

Citrate ions-modified NiFe layered double hydroxide for durable alkaline seawater oxidation

Oxalate anions-intercalated NiFe layered double hydroxide as a highly active and stable electrocatalyst for alkaline seawater oxidation

Benzoate anions-intercalated NiFe-layered double hydroxide nanosheet array with enhanced stability for electrochemical seawater oxidation

NiFe Layered Double Hydroxide/FeOOH Heterostructure Nanosheets As an Efficient and Durable Bifunctional Electrocatalyst for Overall Seawater Splitting

Tungstate Intercalated NiFe Layered Double Hydroxide Enables Long-Term Alkaline Seawater Oxidation

Iron doped Cobalt Nickel Layered Double Hydroxide Supported on Nickel foam as a Robust Electrocatalyst for Highly Efficient Water Oxidation in Alkaline Sea Water

Stabilizing NiFe sites by high-dispersity of nanosized and anionic Cr species toward durable seawater oxidation

A "doping–interfacing" strategy enables efficient alkaline freshwater and seawater oxidation by NiFe-layered double hydroxides

Enhancing the Stability of NiFe-layered Double Hydroxide Nanosheet Array for Alkaline Seawater Oxidation by Ce Doping

MnOx Film-Coated NiFe-LDH Nanosheets on Ni Foam as Selective Oxygen Evolution Electrocatalysts for Alkaline Seawater Oxidation.

Electrodeposition of NiFe-layered double hydroxide layer on sulfur-modified nickel molybdate nanorods for highly efficient seawater splitting

Layered Double Hydroxides with Carbonate Intercalation as Ultra‐Stable Anodes for Seawater Splitting at Ampere‐Level Current Density

Poly(3-thiophenemalonic Acid) Modified NiFe Layered Double Hydroxide Electrocatalyst for Stable Seawater Oxidation at an Ampere-Scale Current Density

Cationic defect-enriched hydroxides as anodic catalysts for efficient seawater electrolysis

Surface-derived Phosphate Layer on NiFe-layered Double Hydroxide Realizes Stable Seawater Oxidation at the Current Density of 1 A°cm−2

Modification of Spinel MnCo2O4 Nanowire with NiFe-layered Double Hydroxide Nanoflakes for Stable Seawater Oxidation

Stable Seawater Electrolysis Over 10 000 H via Chemical Fixation of Sulfate on NiFeBa‐LDH

Poly(phenol red) modified CoFe-layered double hydroxide achieves stable seawater oxidation at an ampere-level current density

Unraveling the crucial contribution of additive chromate to efficient and stable alkaline seawater oxidation on Ni-based layered double hydroxides

N-doped carbon dots coupled NiFe-LDH hybrids for robust electrocatalytic alkaline water and seawater oxidation

NiFe Pyrophosphate Enables Long-Term Alkaline Seawater Oxidation at an Ampere-Level Current Density