Abstract:In this work, carbonate intercalation and etching‐hydrolysis strategies at room temperature and atmospheric pressure are deployed to synthesize the large‐scale and ultra‐stable electrodes for seawater splitting. The as obtained material (NiFe LDH_CO32−) exhibits impressive OER activity under alkaline simulated seawater, showing stable operation for 1000 h at 500 and 1000 mA cm−2. Owing to the presence of a substantial concentration of chlorine in seawater, the anode still faces severe chlorine corrosion, especially the water splitting operated at high current densities. Herein, the cost‐effective and scalable NiFe layered double hydroxides with carbonate intercalation (named as NiFe LDH_CO32−) are synthesized utilizing the etching‐hydrolysis and ion exchange strategies under ambient conditions. Experimental findings demonstrate that NiFe LDH_CO32− shows excellent stability at 500 and 1000 mA cm−2 for 1000 h under alkaline simulated seawater. Additionally, a two‐electrode system offers great stability at current densities ranging from 100 to 1000 mA cm−2 over a duration of 400 h in alkaline seawater. This remarkably catalytic stability can be ascribed to the etching‐hydrolysis and carbonate intercalation strategies. The etching‐hydrolysis strategy leads to an integrated electrode for the catalyst‐carrier, enhancing the adhesion between them, and retarding hence the divorce of catalysts from the carrier. Theoretical calculations suggest that the carbonate intercalation weakens the adsorbability of chlorine on catalysts and hinders the coupling of metal atoms with chlorine, thereby impeding the anode corrosion caused by chlorine and improving catalytic stability. More importantly, this strategy has been extended to the preparation of other layered double hydroxides with carbonate intercalation.

Poly(phenol red) modified CoFe-layered double hydroxide achieves stable seawater oxidation at an ampere-level current density

Oxalate anions-intercalated NiFe layered double hydroxide as a highly active and stable electrocatalyst for alkaline seawater oxidation

Citrate ions-modified NiFe layered double hydroxide for durable alkaline seawater oxidation

Self-protecting CoFeAl-layered double hydroxides enable stable and efficient brine oxidation at 2 A cm −2

Efficient and Stable Neutral Seawater Splitting Achieved Via Strong-Proton-adsorption in Pd-O-Co Collaborative Coordination

Arming Amorphous NiMoO4 on Nickel Phosphide Enables Highly Stable Alkaline Seawater Oxidation.

Tungstate Intercalated NiFe Layered Double Hydroxide Enables Long-Term Alkaline Seawater Oxidation

Efficient and Ultrastable Seawater Electrolysis at Industrial Current Density with Strong Metal‐Support Interaction and Dual Cl−‐Repelling Layers

The cobalt-based metal organic frameworks array derived CoFeNi-layered double hydroxides anode and CoP/FeNi2P heterojunction cathode for ampere-level seawater overall splitting

N-doped carbon dots coupled NiFe-LDH hybrids for robust electrocatalytic alkaline water and seawater oxidation

Surface Anticorrosion Engineering by Polyphosphate Oxyanions for Durable Seawater Oxidation

Stabilizing NiFe sites by high-dispersity of nanosized and anionic Cr species toward durable seawater oxidation

Stable and Efficient Seawater Splitting on a Porous Phosphate-Intercalated NiFe (oxy)hydroxide@nimoo4 Core-Shell Micropillar Electrode

MnOx Film-Coated NiFe-LDH Nanosheets on Ni Foam as Selective Oxygen Evolution Electrocatalysts for Alkaline Seawater Oxidation.

Manipulating anion intercalation into layered double hydroxide for alkaline seawater oxidation at high current density

Layered Double Hydroxides with Carbonate Intercalation as Ultra‐Stable Anodes for Seawater Splitting at Ampere‐Level Current Density

Unraveling the crucial contribution of additive chromate to efficient and stable alkaline seawater oxidation on Ni-based layered double hydroxides

Partially selenized FeCo layered double hydroxide as bifunctional electrocatalyst for efficient and stable alkaline (sea)water splitting

Bimetallic Phosphide Heterostructure Coupled with Ultrathin Carbon Layer Boosting Overall Alkaline Water and Seawater Splitting

Promoting the Corrosion Resistance of Mo‐FeCoP@MnOx/NF via Double Protection Mechanisms Toward Electrolysis of Seawater at Ampere‐Level Current Density

Functional Bimetal Co‐Modification for Boosting Large‐Current‐Density Seawater Electrolysis by Inhibiting Adsorption of Chloride Ions