Dual Cocatalytic Sites Synergize NiFe Layered Double Hydroxide to Boost Oxygen Evolution Reaction in Anion Exchange Membrane Water Electrolyzer
Yue Shi,Lumin Song,Yan Liu,Tiantian Wang,Caixia Li,Jianping Lai,Lei Wang
DOI: https://doi.org/10.1002/aenm.202402046
IF: 27.8
2024-10-23
Advanced Energy Materials
Abstract:For the first time, the Co2.8, W3.8‐NiFe LDH integrated catalyst with dual cocatalytic sites is developed, in which Co and W act as dual cocatalytic sites not only promote the *OH adsorption and protons desorption of Ni(Fe) sites for increasing critical *O coverage, but also regulate the electronic structure of Ni(Fe) sites to reduce the energy barrier of alkaline OER process. Nickel‐iron layered double hydroxide (LDH) is a promising cost‐efficient catalyst to replace noble metals for alkaline oxygen evolution reaction (OER), yet its intrinsic activity under high current density conditions is not satisfactory, which greatly constrains the industrial application of NiFe LDH catalysts. Herein, a new class of integrated Co and W co‐doped NiFe LDH catalysts is reported with dual cocatalytic sites for alkaline OER catalysis. The optimized Co2.8, W3.8‐NiFe LDH integrated catalyst has superior alkaline OER activity (255 mV@1000 mA cm−2) and excellent catalytic stability (200 h@500 mA cm−2). The turnover frequency value of Co2.8, W3.8‐NiFe LDH can reach 4.02 s−1 at 1.49 V versus RHE, which is 9.6 times higher than that of NiFe LDH and superior to the noble metal catalysts. Moreover, it can achieve 1.0 A cm−2 at 1.86 V and maintain 300‐h stable operation in anion exchange membrane water electrolyzer. Theoretical and experimental studies indicate that W sites promote the *OH adsorption and Co sites favor protons desorption of OH*. These dual cocatalytic sites jointly promote *O coverage, effectively accelerating alkaline OER kinetic.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels