Abrasive wear of HDPE/UHMWPE blends

Alessandra de A. Lucas,José D. Ambrósio,Harumi Otaguro,Lidiane C. Costa,José A.M. Agnelli

DOI: https://doi.org/10.1016/j.wear.2011.01.011

IF: 4.695

2011-04-01

Wear

Abstract:Blends of high density polyethylene (HDPE) with ultra-high molecular weight polyethylene (UHMWPE) were obtained by mixing in a melted state at concentrations ranging from 10 to 30% by weight in an intermeshing co-rotating twin screw extruder (ICTSE). The abrasive resistance of the blends was evaluated according to the DIN53516 standard, and it was observed that the volumetric loss of the blends decreased with increasing concentration of UHMWPE. The mechanical properties of the samples were analyzed in terms of flexural, tensile, and impact strength; in general, the HDPE/UHMWPE blends had a good set of properties, most of which were better than the properties of pure HDPE. Thermal analysis of samples was made by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), and no significant difference was observed between the blends and pure HDPE. The morphological analysis conducted by scanning electron microscopy (SEM) showed that the UHMWPE is present in the HDPE matrix as a second phase, but there is a good interface between the two. We found an inverse relationship between the volumetric loss in the abrasive wear of the samples and the product between the tensile strength at yielding and strain at yielding, σyɛy, as proposed by Lancaster and Ratner (Sinha and Briscoe, 2009 [1]).

engineering, mechanical,materials science, multidisciplinary