Abstract:Abstract Tribocorrosion is a failure phenomenon which involves synergistic effect of electrochemical corrosion and mechanical wear. It usually results into early failure of mechanical components than simple wear and corrosion. Chloride (Cl − ) and sulfate ions SO 4 2 − are often found together in corrosive media. In this study, the synergistic effect of Cl − and SO 4 2 − on tribocorrosion of 316L stainless steel was studied by changing the ratio of SO 4 2 − /Cl − in corrosive solution from 0.31 M : 0 to 0 : 0.62 M. The stainless steel was worn against with a ZrO 2 sphere. The coefficient of friction (COF), material loss volume, surface micro-topographies and surface chemical composition in different solutions were compared to explore the synergism between SO 4 2 − and Cl − . The results indicated that the mix of Cl − and SO 4 2 − reduced material loss volume by a quarter when compared with that in pure Na 2 SO 4 or NaCl solution. More than half of material loss was caused by the synergism between wear and corrosion in mixing solutions. The synergistic effect between SO 4 2 − and Cl − could promote the transmission of metal into oxides. This had two effects on tribocorrosion. First, the existence of oxides would cause abrasion which accelerated wear-affected corrosion and enhanced mechanical wear (corrosion-affected wear). On the other side, the transmission of metal into oxides benefited for the formation of tribo-film. The flexible stainless steel needed to coordinate deformation with the tribo-film which had relatively low deformability. This aggravated deformation of stainless steel and promoted surface work-hardening effect. It was helpful for stainless steel to resist wear, thus, the corrosion-affected wear was decreased.

Tribocorrosion behavior of 316L stainless steel sliding against different ceramics in 0.5 M H2SO4 solution

The Effect Of Ceramic Friction Pairs On The Tribocorrosion Behavior Of Aisi 304 Stainless Steel In Seawater

Wear Behavior of Al 2 O 3 -Ticn Composite Ceramic Sliding on Stainless Steel

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Tribocorrosion investigation of 316L stainless steel: the synergistic effect between chloride ion and sulfate ion

Tribological Characteristics of Si3N4 Ceramic Sliding on Stainless Steel

Investigation on the tribological properties of ceramics rubbing against stainless steel at high temperature

Corrosion and Tribocorrosion Behaviors of AISI 316 Stainless Steel and Ti6Al4V Alloys in Artificial Seawater

Effects of Different Cathodic Reactions on Tribocorrosion Behavior of AISI 430 in 0.5 mol/L Sulfuric Acid

Wear Behavior of Si3N4 Ceramic Cutting Tool Material Against Stainless Steel in Dry and Water-Lubricated Conditions

Friction and Wear of Si3N4 Ceramic/stainless Steel Sliding Contacts in Dry and Lubricated Conditions

Tribocorrosion properties of AISI 1045 and AISI 2205 steels in seawater: Synergistic interactions of wear and corrosion

Tribological behaviors of MoAlB ceramic in artificial seawater

Tribological Behavior of Si3N4 - Hbn Ceramic Materials Against Stainless Steel under Dry Friction Condition

Effect of frictional frequency on the subsurface evolution of 316L stainless steel in tribocorrosion and its influence on the synergistic effect between corrosion and wear

Tribological Behaviors of Self‒mated Cu36Zr48Ag8Al8 Bulk Metallic Glass under H2SO4 Conditions with Different Concentrations

Influences of ceramic mating balls on the tribological properties of Cr/a-C coatings with low chromium content in water lubrication

Wear mechanisms of Ti(C, N) ceramic in sliding contact with stainless steel

Exploring the Interplay between Tribocorrosion and Surface Chemistry of the ASTM F139 Surgical Stainless Steel in Phosphate-Buffered Saline Solution

Tribological behaviour of TiB2-HfC ceramic tool material under dry sliding condition

Tribological characteristics of Si3N4–hBN ceramic materials sliding against stainless steel without lubrication