Abstract:The densification of solid wood is a well-studied technique that aims to increase the strength and hardness of the material by permanently compressing the wood tissue. To optimise the densification process in this study, a pre-treatment with sodium sulphite was used (delignification). With delignification prior to densification, one achieves higher compression ratios and better mechanical properties compared to densification without pre-treatment. The reactivity of syringyl (dominant in hardwoods) and guaiacyl (dominant in softwoods) lignin towards delignification is different. The influences of this difference on the delignification and densification of softwoods and hardwoods need to be investigated. This study aimed to densify wood after delignification and investigate how variations in chemical composition between coniferous and deciduous species affect the densification process. Scots pine and Eurasian aspen specimens with a similar initial density were investigated to study the influence of the different lignin chemistry in softwoods and hardwoods on the densification process. Both timbers were delignified with sodium sulphite and sodium hydroxide and subsequently densified. While the delignification was twice as efficient in aspen than in pine, the compression ratios were almost identical in both species. The Brinell hardness and compressive strength showed a more significant increase in aspen than in Scots pine; however, one exception was the compressive strength in a radial direction, which increased more effectively in Scots pine. Scanning electron microscopy (SEM) revealed the microstructure of densified aspen and Scots pine, showing the crushing and collapse of the cells.

Effect of fire-retardant treatment of wood prior to thermo-mechanical densification

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Effect of High-pressure Densification on Moisture Sorption Properties of Paulownia Wood

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Effects of different incising pretreatments in improving permeability in two refractory wood species

Fire resistance of pine wood treated with phenol-formaldehyde resin and phosphate-based flame retardant

Densification of Delignified Wood: Influence of Chemical Composition on Wood Density, Compressive Strength, and Hardness of Eurasian Aspen and Scots Pine

Modification of wood via biochar particle impregnation

Effective strategy for fabricating surface impregnated and unilaterally densified wood with furfuryl alcohol/flame retardants for enhanced mechanical performance and flame retardancy

The Effect of Intumescent Coating Containing Expandable Graphite onto Spruce Wood

Combustion Behavior and Thermal Degradation Properties of Wood Impregnated with Intumescent Biomass Flame Retardants: Phytic Acid, Hydrolyzed Collagen, and Glycerol

Effect of Water Repellents on Hygroscopicity and Dimensional Stability of Densified Fir and Aspen Woods

Flame Retardancy of Densified Wood Modified by Bio-Material Based Flame Retardant

Phosphorus–Nitrogen Interaction in Fire Retardants and Its Impact on the Chemistry of Treated Wood

Exploratory study on the bending performance of thermo-hydro-mechanically densified Scots pine (Pinus sylvestris L.) at elevated temperatures

Effect of superheated steam pressure on the physical and mechanical properties of sandwich-densified wood

Fixation of Tripotassium Citrate Flame Retardant Using a Sorbitol and Citric Acid Wood-Modification Treatment

Effect of Expandable Graphite Flakes on the Flame Resistance of Oak Wood

Densification of poplar veneer

A flame-retardant densified wood as robust and fire-safe structural material