Abstract:This paper reports the development of a physics-based life prediction model that incorporates three micro-damage processes. Both the particle area fraction and size, as determined using scanning electron microscopy, are used as the model input to predict the precipitate coarsening damage. Moreover, the carbon concentration profile, as measured using electron probe micro-analyser, are used to derive the carburisation damage distribution index. Compared to the Kowalewski-Dyson model, the present model can predict the stress dependent creep fracture strain and rupture time. The model, compiled into finite element via the user subroutine, can predict the heterogeneous damage accumulation of the cracking furnace tube made of HP40Nb alloy in a coupled creep-carburisation environment. The predicted total damage is comprised of precipitate coarsening and carburisation as the predominance, while the creep cavitation contributing much less due to the low internal pressure. The distribution of the precipitate coarsening is relatively homogeneous through the thickness, whereas the carburisation causes a steep increased damage value close to the inner surface. With regard to time, the precipitate coarsening damage is predominant in the initial stage, while the total damage is governed by the carburisation process with further exposure. Eventually, the total damage reaches the critical value at 59600 h, with the thickness of carburised layer exceeding 50% of the tube thickness, and the tube fails in the inner surface which agrees with the operational experience. The parametric sensitivity study reveals the importance of determining the Cr-rich carbide area fraction for the life prediction.

A life prediction model for P110S steel in deep-well environments with H 2 S/CO 2 coexistence based on multi-factor chemometric drive

The development of a mechanistic-chemometrics model with multi-degree of freedom for pitting corrosion of HP-13Cr stainless steel under extremely oilfield environments

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

A Probabilistic Model For Corrosion Prediction Of Steel Reinforcement

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

Main control factors and prediction model of flow-accelerated CO2/H2S synergistic corrosion for X65 steel

Corrosion fatigue life prediction model for 10CrNiCu shipbuilding steel under authentic marine environments

Modeling of Corrosion Pit Growth for Prognostics and Health Management.

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Prediction of Crack Initiation Life Due to Corrosion Pits

Fatigue Life Prediction of High Strength Steel with Pitting Corrosion under Three-Point Bending Load

Multi-Physics Coupling Analysis on the Time-Dependent Localized Corrosion Behavior of Carbon Steel in CO2-H2O Environment

Probabilistic constitutive model for corroded structural steel with stochastic pits under monotonic tension

A hybrid probabilistic-deterministic framework for prediction of characteristic size of corrosion pits in low-carbon steel following long-term seawater exposure

A physics-based life prediction model of HP40Nb heat-resistant alloy in a coupled creep-carburisation environment

A Simplified Maximum Pit Depth Model of Mild and Low Alloy Steels in Marine Immersion Environments

Predictive Model for Corrosion Rate of Oil Tubes in CO2/H2 S Coexistent Environment Part Ⅰ :Building of Model

Long-term state-driven atmospheric corrosion prediction of carbon steel in different corrosivity categories considering environmental effects

Numerical Predictions of Mild-Steel Corrosion in A H2s Aqueous Environment Without Protective Product Layers

A Model To Predict The Stress Corrosion Cracking Growth Rate Of The Metallic Materials