High-entropy thermal barrier coating of rare-earth zirconate: A case study on (La0.2Nd0.2Sm0.2Eu0.2Gd0.2)2Zr2O7 prepared by atmospheric plasma spraying

Lin Zhou,Fei Li,Ji-Xuan Liu,Qing Hu,Weichao Bao,Yue Wu,Xueqiang Cao,Fangfang Xu,Guo-Jun Zhang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.07.061
IF: 5.7
2020-12-01
Journal of the European Ceramic Society
Abstract:We report a double-ceramic-layer (DCL) thermal barrier coating (TBC) with high-entropy rare-earth zirconate (HE-REZ) as the top layer and yttria stabilized zirconia (YSZ) as the inner layer sprayed on Ni-based superalloy by atmospheric plasma spraying. La2Zr2O7 (LZ) was selected as a reference for the HE-REZ. Thermal cycling test results demonstrate that the HE-REZ/YSZ DCL coating exhibited obviously improved thermal stability when compared to the LZ/YSZ DCL coating. The reasons for the improvement of the thermal shock resistance are considered to be the anti-sinterability of the HE-REZ ceramics during the thermal cycling test attributed to the sluggish diffusion effect and as well as the better match in the coefficient of thermal expansion of HE-REZ coating with the YSZ inner layer. In addition, the HE-REZ coating maintains fluorite structure after thermal cycling test. This study makes one step forward in the development and application of high-entropy rare-earth zirconate ceramic thermal barrier coatings.
materials science, ceramics
What problem does this paper attempt to address?
The problem this paper attempts to address is the development of a high-entropy rare earth zirconate thermal barrier coating (HE-REZ) to improve the thermal stability and thermal shock resistance of existing thermal barrier coatings (TBC). Specifically, the researchers prepared a double ceramic layer (DCL) structured thermal barrier coating using atmospheric plasma spraying technology, where high-entropy rare earth zirconate (HE-REZ) serves as the top layer and yttria-stabilized zirconia (YSZ) as the inner layer. The paper evaluates the performance of the HE-REZ coating in high-temperature cyclic tests by comparing it with traditional lanthanum zirconate (LZ) coatings and analyzes the reasons for its improved thermal stability. The main research background includes: 1. **Importance of thermal barrier coatings**: Thermal barrier coating systems are an indispensable part of advanced gas turbines, used to protect internal metal components from overheating, thereby extending their service life and increasing operating temperatures. 2. **Limitations of existing materials**: The most advanced thermal barrier coating material currently is yttria-stabilized zirconia (YSZ), but its long-term use temperature limit is 1200°C, and it has issues with high thermal conductivity and phase transformation degradation. 3. **Advantages of high-entropy materials**: High-entropy materials are considered promising alternatives to YSZ due to their low thermal conductivity, high-temperature stability, and resistance to sintering. The main objectives of the research are: - To prepare and characterize high-entropy rare earth zirconate (HE-REZ) coatings. - To evaluate the thermal stability of HE-REZ coatings in high-temperature cyclic tests. - To analyze the mechanisms of improved thermal stability of HE-REZ coatings, particularly their resistance to sintering and thermal expansion coefficient compatibility with the YSZ inner layer. Through this research, the paper aims to promote the development and application of high-entropy rare earth zirconate ceramic thermal barrier coatings.