High-entropy pyrochlores with low thermal conductivity for thermal barrier coating materials

Fei Li,Lin Zhou,Ji-Xuan Liu,Yongcheng Liang,Guo-Jun Zhang

DOI: https://doi.org/10.1007/s40145-019-0342-4

IF: 11.534

2019-07-25

Journal of Advanced Ceramics

Abstract:High-entropy pyrochlore-type structures based on rare-earth zirconates are successfully produced by conventional solid-state reaction method. Six rare-earth oxides (La2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, and Y2O3) and ZrO2 are used as the raw powders. Five out of the six rare-earth oxides with equimolar ratio and ZrO2 are mixed and sintered at different temperatures for investigating the reaction process. The results demonstrate that the high-entropy pyrochlores (5RE1/5)2Zr2O7 have been formed after heated at 1000°C. The (5RE1/5)2Zr2O7 are highly sintering resistant and possess excellent thermal stability. The thermal conductivities of the (5RE1/5)2Zr2O7 high-entropy ceramics are below 1 W·m–1·K–1 in the temperature range of 300–1200°C. The (5RE1/5)2Zr2O7 can be potential thermal barrier coating materials.

materials science, ceramics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop new thermal barrier coating (TBC) materials, especially high - entropy pyrochlore - structure ceramic materials with low thermal conductivity and excellent high - temperature stability. Specifically, the research aims to prepare high - entropy pyrochlore - structure ceramics based on rare - earth zirconates by the solid - state reaction method and evaluate their potential as thermal barrier coating materials.

### Background problems:
1. **Limitations of existing TBC materials**: The most commonly used TBC material at present is yttria - stabilized zirconia (YSZ), but its long - term use temperature upper limit is 1200 °C, because above this temperature, YSZ has a relatively high thermal conductivity and the tetragonal phase is unstable.
2. **Demand for new materials**: In order to improve the performance and lifespan of high - temperature equipment such as turbine engines, it is necessary to develop new materials that can still maintain low thermal conductivity and good stability at higher temperatures (such as above 1300 °C).

### Research objectives:
- **Prepare high - entropy pyrochlore - structure ceramics**: Select six rare - earth oxides (La₂O₃, Nd₂O₃, Sm₂O₃, Eu₂O₃, Gd₂O₃ and Y₂O₃) and ZrO₂, mix them in an equimolar ratio and sinter them to form a high - entropy pyrochlore - structure (5RE₁/₅)₂Zr₂O₇.
- **Evaluate material properties**: Study the thermal conductivity, sintering properties and high - temperature stability of these high - entropy pyrochlore - structure ceramics and verify their feasibility as potential TBC materials.

### Main findings:
- **Successful synthesis of high - entropy pyrochlore**: A single - phase high - entropy pyrochlore - structure (5RE₁/₅)₂Zr₂O₇ was successfully synthesized at 1000 °C.
- **Low thermal conductivity**: In the range of 300 to 1200 °C, the thermal conductivity is lower than 1 W·m⁻¹·K⁻¹, much lower than that of traditional YSZ materials.
- **Excellent high - temperature stability**: These materials exhibit good sintering resistance and high - temperature stability. Even after aging at 1300 °C for 24 hours, they still maintain a stable microstructure and phase composition.

In summary, this research has solved the limitations of current TBC materials in high - temperature applications, proposed a new type of high - entropy pyrochlore - structure ceramic material with low thermal conductivity and excellent high - temperature stability, and provided a new direction for the research and development of next - generation TBC materials.