Fabrication and characterization of high entropy pyrochlore ceramics

Branko Matović,Dejan Zagorac,Ivana Cvijović-Alagić,Jelena Zagorac,Svetlana Butulija,Jelena Erčić,Ondrej Hanzel,Richard Sedlák,Maksym Lisnichuk,Peter Tatarko

DOI: https://doi.org/10.1016/j.bsecv.2021.11.002

IF: 3.483

2021-11-01

Boletín de la Sociedad Española de Cerámica y Vidrio

Abstract:High-entropy rare-earth (RE) zirconates with pyrochlore structure were successfully fabricated by pressureless and spark plasma sintering. RE2Zr2O7 compound with nominal composition (La0.2Y0.2Gd0.2Nd0.2Sm0.2)Zr2O7 was prepared by simple glycine nitrate procedure (GNP). GNP process yielded powders with low crystallinity and after subsequent calcination, well crystalline ceramics were formed. During calcination defective fluorite (F-RE2Zr2O7) and crystal pyrochlore (Py-RE2Zr2O7) structures coexist. Formation of pure crystalline pyrochlore occurs after sintering at 1450°C. High-density ceramics, free of any additives, were obtained after powders compaction and pressureless (PS), as well as field assisted sintering technique (FAST) at 1450°C. Theoretical investigations of the high-entropy RE2Zr2O7 pyrochlore systems were performed. Unit cell parameter of the obtained Py-RE2Zr2O7 is 10.5892(2)Å and 10.5999(2)Å for PS and FAST sintering, respectively, which is in good agreement with the results of Density Functional Theory (DFT) calculations. The thermal diffusivity of sintered samples at room temperature was ∼0.7mm2/s for both sintering methods.