Abstract:A wire arc additive manufacturing system, based on cold metal transfer technology, was utilized to manufacture the Al-Mg alloy walls. ER5556 wire was used as the filler metal to deposit Al-Mg alloys layer by layer. Based on the orthogonal experiments, the process parameters of the welding current, welding speed and gas flow, as well as interlayer residence time, were adjusted to investigate the microstructure, phase composition and crystal orientation as well as material properties of Al-Mg alloyed additive. The results show that the grain size of Al-Mg alloyed additive becomes smaller with the decrease of welding current or increased welding speed. It is easier to obtain the additive parts with better grain uniformity with the increase of gas flow or interlayer residence time. The phase composition of Al-Mg alloyed additive consists of α-Al matrix and γ (Al12Mg17) phase. The eutectic reaction occurs during the additive manufacturing process, and the liquefying film is formed on the α-Al matrix and coated on the γ phase surface. The crystal grows preferentially along the <111> and <101> orientations. When the welding current is 90 A, the welding speed is 700 mm/min, the gas flow is 22.5 L/min and the interlayer residence time is 5 min, the Al-Mg alloy additive obtains the highest tensile strength. Under the optimal process parameters, the average grain size of Al-Mg alloyed additive is 25 μm, the transverse tensile strength reaches 382 MPa, the impact absorption energy is 26 J, and the corrosion current density is 3.485 × 10−6 A·cm−2. Both tensile and impact fracture modes of Al-Mg alloyed additive are ductile fractures. From the current view, the Al-Mg alloys manufactured by WAAM-CMT have a better performance than those produced by the traditional casting process.

Metallurgical and mechanical properties of marine grade AA5356 using wire arc additive manufacturing

Mechanical Properties, Microstructural Characteristics and Heat Treatment Effects of WAAM Stainless-Steel Plate Material

Microstructure and Mechanical Properties of 304L Steel Fabricated by Arc Additive Manufacturing

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Printing High-Strength High-Elongation Al4043 Alloy Using UNS A94043 Welding Wires through Wire Arc Additive Manufacturing

Microstructural and Defect Evolution during WAAM Resulting in Mechanical Property Differences for AA5356 Component

Characterization of 5356 Aluminum Walls Produced by Wire Arc Additive Manufacturing (WAAM)

Surface Characteristics, Microstructural, and Tribological Behavior of Wire Arc Additive Manufactured Aluminum-5356 Alloy

Arc Additively Manufactured 5356 Aluminum Alloy with Cable-Type Welding Wire: Microstructure and Mechanical Properties

Microstructural and mechanical properties analysis of SS 316L structure fabricated using CMT-wire arc additive manufacturing

Mechanical, metallurgical, and corrosion investigations on wire arc additively manufactured low carbon steel

The Fracture Toughness and Fatigue Crack Growth Properties of 18ni 300 Maraging Steel Manufactured by Wire + Arc Additive Manufacturing

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Mechanical Performance and Failure Mechanism of Layered Walls Produced by Wire Arc Additive Manufacturing in Metal Transfer Pulsed Mode

Microstructure and mechanical properties of the wire arc additively manufactured 316L/ER70S-6 bimetal structure

Fabrication of Bimetallic Structure (SS 316L/SS 308L) via Wire + Arc Additive Manufacturing: A Detailed Characterization of Interface

Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Fabricated by Wire and Arc Additive Manufacturing

Mechanical Properties and Microstructural Characteristics of Al–Mg Alloy Cylindrical Component Manufactured by Wire Arc Additive Manufacturing Process

Wire Arc Additive Manufactured Mild Steel and Austenitic Stainless Steel Components: Microstructure, Mechanical Properties and Residual Stresses

Wire Arc Additive Manufacturing (WAAM) of Aluminum Alloy AlMg5Mn with Energy-Reduced Gas Metal Arc Welding (GMAW)

Experimental study of shielding gas concentration on mechanical properties of stainless steel alloy parts using wire and arc additive manufacturing