Metallurgical and Corrosion Characterization of Austenitic Stainless Steel Welds during Post Weld Heat Treatment
Liamine Kaba,Ahmed Kellai,Said Dehimi,Sami Kahla,Zoheir Boutaghou,Tarek Bendris
DOI: https://doi.org/10.1007/s11665-024-09973-8
IF: 2.3
2024-08-29
Journal of Materials Engineering and Performance
Abstract:In this study, the effects of post weld heat treatment (PWHT) on the microstructure evolution, mechanical properties and corrosion resistance of 304 austenitic stainless steel (ASS) welds generated via the gas tungsten arc welded (GTAW) process were investigated. Weldments were subjected to PWHT at 650, 850 and 1050 °C for 1 h, followed by water quenching. Optical and scanning electron microscopy revealed equiaxed austenite grains ( γ ) limited by grain boundaries in the microstructure of the base metal (BM). A minor content of delta ferrite ( δ ) was observed at the grain boundaries, accompanied by twin crystals distributed within the austenitic matrix. Subjecting the ASS weld to PWHT at 650 °C caused the microstructure to partially recrystallize. By contrast, PWHT at 850 °C induced the formation of new small γ -grains, which was attributed to recrystallization with coarser γ -grains; this effect was particularly pronounced for PWHT at 1050 °C. The microstructure of the weld zone (WZ) remained unchanged by PWHT at all temperatures, predominantly retaining a dendritic structure containing skeletal δ -ferrite. As the temperature of the heat treatment was increased, the distribution of δ -ferrite became increasingly more uniform (particularly for treatment at 650 °C), accompanied by an increase in the width of δ -ferrite dendrites. The microhardness profiles indicated a phase instability, where the Vickers microhardness of the WZ (approximately 150 ± 10 HV) was lower than that of the BM. The highest ultimate tensile strength (UTS) observed in the as-welded joint was 670.2 MPa, but the highest elongation (E) of 20.87% occurred in the sample subjected to PWHT at 650 °C. Subjecting samples in a 3.5 wt.% NaCl solution to PWHT up to 850 °C improved the corrosion resistance of the WZ. By contrast, the as-welded BM samples exhibited greater corrosion resistance than the heat-treated samples did.
materials science, multidisciplinary