Influence of Microstructure on Corrosion Properties of Fe–V Alloy from Vanadium Slag

Weibin Wang,Wei Wang,Qirui Sun
DOI: https://doi.org/10.1007/s12540-023-01523-6
IF: 3.451
2023-09-11
Metals and Materials International
Abstract:Four types of multiphase Fe–V alloys were examined, comprising ferrite, pearlite, and bainite microstructures. Electrochemical impedance spectroscopy and potentiodynamic polarization were employed to study the effect of microstructure on electrochemical properties of the alloys in 3.5% NaCl solution. The cathode reaction was found to be the main step controlling the corrosion dissolution process. The lowest corrosion current density (2.104 μA/cm 2 ) for the Fe–V alloy with bainite indicated that it had outstanding corrosion resistance. Although an increase in pearlite content had a negative effect on corrosion resistance of the alloy, refinement of the lamellar spacing had the opposite effect. Surface corrosion morphologies were observed by scanning electron microscopy. The results indicate that fine cementite uniformly distributed in the bainite promoted slight uniform dissolution of ferrite. Corrosion and dissolution that occurred at the junctions of the pearlite colonies with different directions was more severe. The increase of content of V effectively improved the corrosion resistance of Fe–V alloy. Compared with the matrix, the VC precipitated phase was cathodically protected in the electrochemical corrosion process by virtue of its positive corrosion potential. Graphical
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?