Abstract:Polyimide (PI) films have excellent comprehensive properties and bright prospects in the next generation of optoelectronic and microelectronic applications. PIs were synthesized by aromatic diamines and alicyclic dianhydrides considered to be the most effective method for preparing polyimides with high light transmittance and low dielectric constant. In order to improve the overall performance of polyimide, the introduction of a large trifluoromethyl group into the main chain is also considered a powerful strategy. In this article a novel diamine containing 6 trifluoromethyl groups has been designed and synthesized by Suzuki reaction. Afterwards, PIs were synthesized with fluorinated aromatic dianhydride and alicyclic dianhydride through a two-step method. The two PIs have excellent solubility: PI-a and PI-b exhibited excellent solubility in common polar solvents. Such as DMF, DMAc, NMP and DMSO at room temperature, and PI-a was soluble in low-boiling solvents such as ethyl acetate, CH2Cl2 and CHCl3 at room temperature. PI-b was soluble in low-boiling solvents acetone and CHCl3 at room temperature, which was rarely seen in other aromatic polyimides. Soluble in common organic solvents, especially low boiling point solvents, made these polymers easy to process and suitable for processing technology in solution. This was an important modification for PIs. They also showed good high temperature resistance: the decomposition temperature (T5%) of two PIs were 520 °C and 475 °C. In addition, the residual rate at 790 °C was 50 % and 49 % respectively. Two PI films had a very low dielectric constant 2.26 and 2.24, respectively, which was attributed to the hyperbranched structure and strong electron-withdrawing fluorine-containing groups. PI-a and PI-b also had low water absorption of 0.66 % and 0.72 %, respectively. The transmittance of PI-a and PI-b high transparent films at 450 nm were 74% and 82%, respectively. The significant optical modification was mainly due to the weak electron-accepting alicyclic unit and the large trifluoromethyl electron withdrawing group. This work mainly provided an effective strategy for synthesizing comprehensive excellent performance PIs with high transmittance, excellent solubility, low water absorption, high heat resistance and low dielectric constant.

Rapid, Mild Synthesis of Transparent Polyimides with High Refractive Index via Thiol-Michael Click Reaction

Highly Refractive Polyimides Derived from Efficient Catalyst-Free Thiol–Yne Click Polymerization

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Preparation and characterization of organic soluble polyimides with low dielectric constant containing trifluoromethyl for optoelectronic application

Catalyst-Free Thiol–Yne Click Polymerization: A Powerful and Facile Tool for Preparation of Functional Poly(vinylene Sulfide)s

Organosoluble polyimides with low dielectric constant prepared from an asymmetric diamine containing bulky m-trifluoromethyl phenyl group

Synthesis and properties of novel colorless and thermostable polyimides containing cross‐linkable bulky tetrafluorostyrol pendant group and organosoluble triphenylmethane backbone structure

Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Transparent and highly organosoluble aromatic polyimides with twisted backbone and bulky side substituents for flexible substrate materials

Preparation of Meldrum's Acid‐functionalized Polyimides Exhibiting Organo‐soluble, Reactive, Self‐crosslinkable, and Colorless Features

Synthesis of UV-resistant and colorless polyimide films for optoelectrical applications

Super-heat resistant, transparent and low dielectric polyimides based on spirocyclic bisbenzoxazole diamines with Tg > 450 °C

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Colorless transparent and thermally stable terphenyl polyimides with various small side groups for substrate application

Design, Synthesis and Properties of Semi-Alicyclic Colorless and Transparent Polyimide Films with High Glass Transition Temperatures and Low Retardation for Potential Applications in Flexible Electronics

Effect of orientation of phosphinate pendant on the transparency of polyimides: Design and synthesis of phosphinated diamines with a bulky ortho substitution for high-Tg, transparent polyimides

Synthetic strategies for highly transparent and colorless polyimide film

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Terphenyl-based Colorless and Heat-resistant Polyimides with Controlled Molecular Structure by Methyl Side Groups

One-pot Aqueous-Phase Synthesis of Polyimides from Typical Monomers

From Molecular Design to Practical Applications: Strategies for Enhancing the Optical and Thermal Performance of Polyimide Films