Abstract:The thermal oxide layer formed of TA15 alloy has poor corrosion resistance. In this paper, the changes of the elements and components on the surface after laser ablation with different energy densities (E) were researched. The formation process and corrosion behavior of laser-generated oxide layer were clarified. As E increases, the oxygen content decreases from 8.52% to 5.43% and then increases to 11.89%. The surface oxide layer changes from TiO2(R) (i.e., rutile) to Ti2O3 + TiO2(R) and finally becomes TiO2(R) + TiO2(A) (i.e., anatase). The TiO2(R) gasification was confirmed by calculating the surface temperature rise. The surface reoxidation process was illustrated by a thermodynamically calculated ∆G-T(i.e., the Gibbs free energy changes with temperature). When E ≥ 17.5 J·cm−2, the oxide layer exhibits an agitated morphology, and oxide falls off at the bottom. As E increases, the corrosion rate decreases first and then increases. With energy density of 8.75 J·cm−2, the surface corrosion rate was 20.43 times slower than that of the untreated sample. The impedance spectrum and equivalent resistance results also prove the best corrosion resistance at 8.75 J·cm−2. The corrosion behavior of the oxide layer is analyzed from the properties of the oxide layer components and the reaction products with the electrolyte.<h3 class="a-plus-plus">Graphic abstract</h3>

High-Temperature Oxidation Behaviors of TA15 Titanium Alloy after Mechanical Grinding and Laser Cleaning

Removal mechanism of surface cleaning on TA15 titanium alloy using nanosecond pulsed laser

Ablation oxidation and surface quality during laser polishing of TA15 aviation titanium alloy

Surface Characterization of Thermally Oxidized Titanium Alloys

Modification of TA15 alloy surface by high-pulse-frequency laser cleaning

Removal Mechanism of Liquid-Assisted Nanosecond Pulsed Laser Cleaning TA15 Titanium Alloy Oxide Film

Nanosecond pulsed laser cleaning of titanium alloy oxide films: Modeling and experiments

Effect of laser fluence on the cleaning quality and surface properties of TA15 titanium alloy surface paint layer

Finite Element Simulation of Temperature Field in Laser Cleaning of TA15 Titanium Alloy Oxide Film

Reoxidation process and corrosion behavior of TA15 alloy by laser ablation

Effect of galvanometer scanning speed on the cleaning quality of anodic oxide film on TC2 titanium alloy surface in laser cleaning

Laser cleaning for inorganic thermal control coatings on aluminum alloys: Microstructure evolution and mechanical properties of substrate

Surface and Property Characterization of Laser Polished Ti6Al4V

Correction To: Study on Surface Quality of Laser Cleaning of Oxide Film on Nickel-Base Superalloy

Enhancing the corrosion properties and microhardness of titanium alloy by laser surface remelting

Effects of laser polishing on surface morphology and mechanical properties of additive manufactured TiAl components

Effect of Energy Distribution on Laser Cleaning Quality of 30cr3 Ultra-High Strength Steel

High-temperature oxidation behaviour of Ti65 titanium alloy fabricated by laser direct energy deposition

Improvement in Oxidation Resistance of Ti2AlNb Alloys at High Temperatures by Laser Shock Peening

Laser Texturing for Superwetting Titanium Alloy and Investigation of Its Erosion Resistance

Investigation on mechanism of oxide removal and plasma behavior during laser cleaning on aluminum alloy