Abstract:The results of a study of the influence of the introduction of powders of intermetallic compounds of various compositions obtained by self-propagating high-temperature synthesis (SHS) with preliminary mechanical activation on the structure, mechanical, and tribological properties of sintered bronze are presented. It was found that the introduction of 0.2–0.5 wt % of nickel and titanium aluminides, both single-phase and two-phase, leads to an increase in the density and strength of sintered bronze; maximum strength is achieved with the introduction of 0.2 wt % aluminides. The dependence of the hardness of powder bronze on the amount and composition of the intermetallic compound differs from the dependence of strength; with the introduction of single-phase intermetallic compounds, the hardness increases with increasing additive content, and with two-phase intermetallic compounds it decreases. It has been shown that the introduction of aluminides ensures a refinement of the structure of the bronze during sintering, and at an additive content of 1 wt %, an increase in the amount of eutectoid (α + δ). The introduction of aluminides also has a positive effect on the tribological properties of sintered bronze. With the introduction of 0.5 wt % two-phase nickel aluminide and 0.2 wt % single-phase titanium aluminide, the seizure pressure and wear resistance increase by 2.8 times and 3.5 times, respectively. Adding 0.5 wt % of single-phase nickel, titanium, and iron aluminides allows reducing the friction coefficient to 0.009–0.011, and two-phase iron aluminide to 0.005. The introduction of iron aluminides most effectively increases the tribological properties of sintered bronze, so the seizure pressure increases to 10 MPa and wear resistance by almost 10 times. Aluminides help reduce the relief of the friction surface during adhesive wear of sintered bronze and the formation of microlacunae, which are additional reservoirs for lubrication. The smoothest friction surface and a higher content of microlacunae are observed in samples made of powder bronze with the addition of single-phase iron aluminide.

Preparation of Bronze (CuSn10) Parts by Material Extrusion Process Using Paraffin-Based Binder

Effect of powder characteristics on the microstructure and performance of CuSn10 parts by material extrusion 3D printing

Microstructural Characteristics and Mechanical Properties of Bronze/steel Bimetallic Laminated Composite Prepared by Protective Atmosphere Casting Process

Influence of Binder Composition and Material Extrusion (MEX) Parameters on the 3D Printing of Highly Filled Copper Feedstocks

Enhancing thermal conductivity of sinterized bronze (Cu89/Sn11) by 3D printing and thermal post-treatment: Energy efficiency and environmental sustainability

Microstructure and Properties of Tungsten-40 Wt.-% Copper Composites Fabricated by Binder Jet 3D Printing

Experimental investigation of material extrusion additive manufacturing of copper with high powder loading rate

The Preparation and Properties of Thick Bronze Coating Using Friction-Assisted Jet Electrodeposition

Influence of Ultrafine Additives of Intermetallides on the Structure, Mechanical, and Tribotechnical Properties of Sintered Tin Bronze

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Tensile behavior of a bi-layered bronze/steel sheet: Synergetic effects of microstructure and residual stress

An exploration of binder jetting of copper

A printability evaluation of fine and coarse powder in binder jetting of dense and porous copper parts

Optimization of tin and aluminum content in tin bronze according to mechanical properties indicators

Investigation on mechanical properties of bronze infill PLA composite fabricated by fused deposition modelling

Parameter Optimization and Precision Control of Water-Soluble Support Cores for Hollow Composite Castings Fabricated by Slurry Microextrusion Direct Forming Method

Binder jetting additive manufacturing of 316L stainless-steel green parts with high strength and low binder content: Binder preparation and process optimization

Multi-material bronze-steel plain bearings produced by laser-directed energy deposition

Effect of print orientation and bronze existence on tribological and mechanical properties of 3D-printed bronze/PLA composite

Experimental Study on Metal Parts under Variable 3D Printing and Sintering Orientations Using Bronze/PLA Hybrid Filament Coupled with Fused Filament Fabrication

Copper Plating of Graphite Skeletons Based on Selective Laser Sintering