Effect of tool geometry on the microstructure of friction stir welding of copper and 316L stainless steel

Gautier Huser,Mayerling Martinez Celis,Florent Picot,Peter Minárik,Jozef Veselý,Anne-Laure Helbert,Eric Hug

DOI: https://doi.org/10.1002/adem.202301812

IF: 3.6

2024-02-13

Advanced Engineering Materials

Abstract:In this work, the microstructure evolution during dissimilar Friction Stir Welding of copper with stainless steel 316L was studied. The welding was performed in transparence configuration using tools of two different geometries. The joints were characterized by optical and electron microscopy methods (SEM and TEM), electron backscattered diffraction (EBSD), and microhardness. It was shown that the microstructure and crystallographic texture of base metals are significantly affected by the geometry of the tool. The joint produced using a shoulder of 8 mm in diameter is characterized by a copper nugget with refined grains. The texture of copper, which is for the first time reported for this hybrid welding, is dominated by B / B ̄ component of the simple shear texture. The steel beneath the tool also shows a grain refinement with grains of sub‐micron size and a texture which is close to that of ideal simple shear texture. For the joint produced by the 16 mm diameter tool shoulder, the nugget consists of large grains of copper, while the steel beneath the tool shows small recrystallized grains of micrometer size. The texture in the steel is dominated by the B / B ̄ component of the simple shear texture. The Cu/316L interface in both types of joint is of very good quality, free from microcracks or voids. A detailed study of the interface reveals that the welding between the two dissimilar metals is achieved by their mutual intense mechanical interlocking without formation of any intermetallic compounds. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary