Effect of welding speed on microstructure, nano-mechanical and nano-tribological characteristics of dissimilar friction stir welded AA6061-T6 and AZ31 alloy
Virendra Pratap Singh,Ashish Kumar,Deepak Kumar,Basil Kuriachen,Virendra Pratap SinghAshish KumarDeepak KumarBasil Kuriachena Department of Mechanical Engineering,National Institute of Technology Mizoram,Aizawl,Indiab Department of Mechanical Engineering,IES College of Technology,Bhopal,Indiac Department of Mechanical Engineering,Delhi Technological University,New Delhi,Indiad Department of Mechanical Engineering,Galgotias College of Engineering and Technology,Greater Noida,Indiae Department of Mechanical Engineering,Carnegie Mellon University,Pittsburgh,PA,USAf Department of Mechanical Engineering,National Institute of Technology Calicut,Kozhikode,India
DOI: https://doi.org/10.1080/01694243.2024.2302268
IF: 2.431
2024-01-13
Journal of Adhesion Science and Technology
Abstract:The microstructural, tribological, and mechanical performance of friction-stir welded AA6061-T6 and AZ31 alloys were investigated using electron back scattered diffraction, scanning electron microscope, X-ray diffraction, and electron dispersed spectroscopy methods. The non-destructive X-ray microcomputed tomography test was used to analyse weld porosity. The distribution of volumetric and surface flaws (pores) was found to be confined across the weldment. Using a novel atomic force microscopy method, the nano-tribological characteristics of the base metal and localized regions of welded sample were studied for the first time. The significant difference in wear and friction behaviour was observed in all weld zones and base metal of magnesium side, which was correlated with the hardness of these regions. AFM results showed strong variation in tribological properties in correlation with the hardness trends of different weld zones, i.e. higher hardness leads to low wear. In weldments, intermetallic compounds such as Al 12 Mg 17 and Al 3 Mg 2 were produced, resulting in nanohardness differences as measured by the nanoindentation test. The joint efficiency of 65%, 84%, and 91% were obtained at welding speeds of 16 mm/min, 20 mm/min, and 25 mm/min, respectively.
materials science, multidisciplinary,engineering, chemical,mechanics