Abstract:Titanium alloys face challenges of high temperature oxidation during the service period when used as aircraft engine components. In this paper, the effect of Y2O3 addition on the oxidation behavior and the microstructural change of the Ti6Al4V alloy fabricated by selective laser melting (SLM) was comprehensively studied. The results show that the surface of the Ti6Al4V alloy is a dense oxide layer composed of TiO2 and Al2O3 compounds. The thickness of the oxide layer of the Ti6Al4V increased from 59.55 μm to 139.15 μm. In contrast, with the addition of Y2O3, the thickness of the oxide layer increased from 35.73 μm to 80.34 μm. This indicates that the thickness of the oxide layer formation was a diffusion-controlled process and, therefore, the thickness of the oxide layer increased with an increase in temperature. The Ti6Al4V-1.0 wt.% Y2O3 alloy exhibits excellent oxidation resistance, and the thickness is significantly lower than that of the Ti6Al4V alloy. The oxidation kinetics of the Ti6Al4V and Ti6Al4V-1.0 wt.% Y2O3 alloys at 600 °C and 800 °C follows a parabolic rule, whereas the oxidation of the Ti6Al4V and Ti6Al4V-1.0 wt.% Y2O3 alloys at 1000 °C follows the linear law. The average microhardness values of Ti6Al4V samples after oxidation increased to 818.9 ± 20 HV0.5 with increasing temperature, and the average microhardness values of the Ti6Al4V-1.0 wt.% Y2O3 alloy increases until 800 °C and then decreases at 1000 °C. The addition of Y2O3 shows a significant improvement in the microhardness during the different temperatures after oxidation.

Isothermal oxidation behaviour of TiAl alloys prepared by spark plasma sintering with the addition of Gd under water vapour at 900 °C

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

High-temperature oxidation behaviour of TiAl alloys with Co addition

Oxidation Behavior of TiAl(Cr, Ag) at 900 °C in Water Vapor

High-temperature oxidation behavior and corrosion behavior of high strength Mg-xGd alloys with high Gd content

Non-isothermal Oxidation Characteristic of Titanium-Aluminium Intermetallic Alloys

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Achieving fine-grained Ti-V-Al light weight shape memory alloys with higher transformation temperature, superior performances by doping Gd

Revealing the effect of Gd alloying on oxidation resistance and oxide film protection performance of AZ80 alloy

Microstructure, Hardness and Corrosion Behavior of Ni-Ti Alloy with the Addition of Rare Earth Metal Oxide (Gd2o3)

High-Temperature Oxidation Behaviour of a TiAl-Based Alloy Subjected to Aluminium Hot-Dipping

High Temperature Oxidation Behavior of Additive Manufactured Ti6Al4V Alloy with the Addition of Yttrium Oxide Nanoparticles

Improving the corrosion resistance of MgZn1.2Gd Zr0.18 (x = 0, 0.8, 1.4, 2.0) alloys via Gd additions

Oxidation Resistance of TiAl-Inconel625 Graded Alloying Layer

Influence of water vapour on the oxidation behaviour of TiAl based multielement alloys

Effect of Gd on microstructure, mechanical properties and damping properties of Fe-Cr-Al alloys

Study of microstructure and corrosion resistance of FeCrAl-Gd alloys

Effect of Al addition on microstructure and mechanical properties of Mg−Gd−Zn alloys

Comprehensive Unveiling of the Oxidation Resistance and Corrosion Protection of an Oxide Layer Formed on the Gd-Alloyed AZ80 Alloy Surface

Microstructure and Oxidation Behavior of NiCoCrAlY Coating with Different Sm2O3 Concentration on TiAl Alloy