Abstract:Magnesium aluminate spinel (MgAl2O4) ceramics are high-performance and carbon-free materials widely used in both military and civilian fields. However, it is usually challenging to densify during the solid-state sintering process. The excellent properties of some rare earth oxides have been proved to promote the densification of MgAl2O4 spinel ceramics. But the mechanism of promoting sintering is not clear. In the present work, MgAl2O4 spinel ceramics have been successfully fabricated by co-doping CeO2 and La2O3 via a single-stage solid-state reaction sintering. The effects of addition amounts of CeO2 and La2O3 on phase compositions, microstructures, sintering characteristics, cold compressive strength, and thermal shock resistance of as-prepared MgAl2O4 spinel ceramics were systematically investigated. The results show that by co-doping CeO2 and La2O3 can increase the defect concentration due to the lattice distortion. This could promote the movement of Al3+ and Mg2+ at high temperature, which is beneficial to the formation of more secondary MgAl2O4 spinel. t-ZrO2 with more Ce4+ filling between spinel grains could prevent the growth of grains and promote the densification, besides the new-formed LaAlO3 that was mainly distributed along the grain boundary of the MgAl2O4 phase, both of which were favorable for the formation of dense microstructure of MgAl2O4 spinel materials. At the same time, the formation of more secondary MgAl2O4 spinel and sintering densification also improve the mechanical properties of spinel ceramics. La3+ will segregate to the spinel grain boundary, preventing grain boundary movement and absorbing the main crack's fracture energy. With 3 wt% CeO2 and 3 wt% La2O3 co-doping, the bulk density of the sample increased from 3.02 g∙cm−3 to 3.55 g∙cm−3; the apparent porosity decreased from 12.21% to 9.97%; the cold compressive strength increased from 172.88 MPa to 189.54 MPa; and the residual strength retention ratio after thermal shock increased from 84.92% to 89.15%.

An efficient Yb2O3 additive for improved densification and corrosion resistance of MgAl2O4 spinel

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Effect of Y2O3 on the corrosion resistance of two-step sintered Al5Y3O12-MgAl2O4 sidewalls in the aluminum electrolyte

Effect of Y2O3 and ZnO co-doping on the densification and properties of magnesium aluminum spinel

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Influence of Y2O3 on microstructure, crystallization, and properties of MgO-Al2O3-SiO2 glass-ceramics

Preparation and properties of MgAl2O4 spinel ceramics by double-doped CeO2 and La2O3

Improvement on Corrosion Resistance of Molten Calcium-Magnesium-Alumina-Silicate (cmas) by Yb2o3-Y2o3 Co-Stabilized Zro2 Ceramic Pellets

Effects of Sm2O3 addition on sintering behavior of pre-synthesized magnesia-rich magnesium aluminate spinel

Effect of Eu2O3 on sintering densification and corrosion resistance of magnesium aluminate spinel

Effect of Y2O3 Addition on the Microstructure, Wear Resistance, and Corrosion Behavior of W-4.9Ni-2.1Fe Heavy Alloy

Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Magnesium aluminate spinel transparent ceramics with high optical and mechanical performance by Y3Al5O12 sintering additive

Enhanced thermal shock resistance of hydratable magnesium carboxylate bonded castables via in-situ formation of micro-sized spinel

Effects of different particle size of spinel and Y2O3 additive of the periclase-spinel refractory on the sintering densification and corrosion resistance to copper smelting slag

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Effect Of Y2o3 On Property Of Mullite Ceramic Enhanced By Andalusite

Microstructural and Optical Properties of MgAl2O4 Spinel: Effects of Mechanical Activation, Y2O3 and Graphene Additions

The effect of MnO2 additive on the microstructure and mechanical properties of magnesium aluminate spinel

The microstructure evolution and performance enhancement of MgO-C refractories by the addition of MA90 spinel micro-powder

Enhancing mechanism of improved slag resistance of Al2O3-spinel castables added with pre-synthesized (Al,Cr)2O3 micro-powder