Abstract:Ultrasonic surface rolling processing (USRP) was performed on a Mg–Y–Nd–Zr alloy after equal-channel angular pressing. The result shown that the surface roughness was significantly improved, residual stress was introduced to the topmost surface, and ~450 μm gradient nanostructure (GNS) of Mg alloys was obtained after USRP treatment. The mechanism of microstructure evolution and its effect on the mechanical properties of the Mg alloy were studied in detail. There are multiple deformation mechanisms in grain refinement. In the initial stage, the coarse-grain (CG) matrix was subdivided by {10 1̅ 2} extension twins. Subsequently, the deformed grains were refined into substructures using interaction between twins, interaction between twins and dislocations, and dislocation entanglement. Moreover, the substructure contains a high density of multiple stacking faults and dislocation arrays, which can effectively block dislocation movement and promote dislocation packing. Finally, equiaxed nanograins (NGs) with high-angle grain boundaries were formed via subcrystal rotation recrystallization. With the formation of a GNS, the strength of the Mg–Y–Nd–Zr alloy considerably increased at the expense of a small amount of plasticity. The tensile test results demonstrated that the yield strength (YS) and ultimate tensile strength (UTS) of the Mg–Y–Nd–Zr alloy increased from 171.96 and 262.47 MPa to 216.06 and 330.61 MPa, respectively, and the elongation rate decreased from 20.52% to 14.65% after the USRP treatment. The YS improvement of the Mg–Y–Nd–Zr alloy after the USRP treatment was attributed to grain boundary strengthening, synergistic strengthening, dislocation strengthening, and twin strengthening. Furthermore, the microhardness of Mg–Y–Nd–Zr considerably improved after USRP treatment, and grain refinement was the primary surface strengthening mechanism of the Mg–Y – Nd – Zr alloy after the USRP treatment. The work-hardening capacity of the Mg alloy improved after the USRP treatment, and the synergistic deformation between GNS and CG matrix was the primary reason for the excellent work-hardening capacity of the Mg–Y–Nd–Zr alloy.

Effect of stacking faults in nanograins on the tensile properties of Mg–Y–Nd–Gd–Zr alloys subjected to ultrasonic surface rolling processing

Effect of microstructure evolution on the mechanical properties of a Mg–Y–Nd–Zr alloy with a gradient nanostructure produced via ultrasonic surface rolling processing

Effect of ultrasonic surface rolling process on microstructure and properties of rolled Mg-Y-Nd-Zr alloy

Formation Mechanism of Surface Gradient Microstructure and Mechanical Properties Evolution of Mg-Y-Nd-Gd-Zr Alloy by Ultrasonic Rolling

Microstructures and mechanical properties of Mg-15Gd-1Zn-0.4Zr alloys treated by ultrasonic surface rolling process

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Ultrasonic Surface Rolling Process on Wear Behavior of Mg-15Gd-1Zn-0.4Zr Alloy

Microstructure and Mechanical Properties of AZ31B Magnesium Alloy via Ultrasonic Surface Rolling Process

Microstructure, texture evolution and mechanical anisotropy of Mg-Gd-Y-Zn-Zr alloy sheets produced by unidirectional and cross rolling

The Effect of Morphology of the Long-Period Stacking Ordered Phase on Mechanical Properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) Alloy

Distributions of Grains and Precipitates in Gradient Lamellae Al–Zn–Mg–Cu Alloy by Ultrasonic Surface Rolling Processing

Microstructure and thermal stability of nanocrystalline Mg-Gd-Y-Zr alloy processed by high pressure torsion

Effect of twin assisted precipitation on the microstructure and mechanical properties of gradient structure Mg-Gd-Zn-Zr alloy

Enhanced fatigue resistance and fatigue-induced substructures in an additively manufactured CoCrNi medium-entropy alloy treated by ultrasonic surface rolling process

Effect of Deformation Parameters on Recrystallization Behavior and Long-Period Stacking-Ordered Phase of Mg-9Gd-4Y-2Zn-0.5Zr Alloy

Effect of the interspacing of intragranular lamellar LPSO phase on dynamic recrystallization behaviors of Mg-Gd-Y-Zn-Zr alloys

The effect of grain size on deformation modes and deformation heterogeneity in a rolled Mg-Zn-Ca alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Simultaneously improving tensile properties and stress corrosion cracking resistance of 7075-T6 aluminum alloy by USRP treatment

7075 aluminum alloy induced by ultrasonic surface rolling: grain refinement and residual stress model analysis and evaluation

Microstructure Evolution and Mechanical Properties of Mg-10.37Gd-3.66Y-2.27Zn-0.52Zr Alloy during Reciprocating Upsetting-Extrusion