Abstract:In this study, Ti–Si–C composite coatings were synthesized via plasma spraying of agglomerated powders prepared by a spray drying/precursor pyrolysis technology using Ti, Si, and sucrose powders. The influence of Si content, ranging from 0 wt% to 24 wt%, on the microstructure, mechanical properties, and oxidation resistance of the composite coatings was investigated. Results show that the phase composition of the Ti–Si–C composite coatings changes with the increasing Si content. The coatings without Si addition consist of TiC and Ti3O; the coatings with 6–18 wt% Si are composed of TiC, Ti5Si3, and Ti3O; the coatings with Si content of 24 wt% form only TiC and Ti5Si3 phases. As the Si content increases, the hardness of the Ti–Si–C composite coatings increases first and then decreases, depending on the intrinsic hardness of the ceramic phases, the brittleness of Ti5Si3, and the defects such as pores and cracks. The Ti–Si–C composite coatings have high wear resistance due to the in-situ synthesized high-hardness TiC and Ti5Si3. Owing to the high brittleness of Ti5Si3, the increasing Si content leads to higher wear volume loss at room temperature, which can be partially improved in high-temperature wear tests. The oxidation resistance of Ti–Si–C composite coatings increases with the increase of Si content, and the higher the oxidation temperature, the more obvious the influence of the Si addition on oxidation resistance.

Effect of Si content on the oxidation behavior of CoCrWSi coatings at 900 °C

High Temperature Oxidation Behavior of Co-20Re-25Cr-2Si Alloy at Different Oxygen Pressures

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Effect of Si on the structure and oxidation behavior of Cr-Si coatings on Zry-4 under high temperature steam environment

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

Study on the high-temperature oxidation of AlCrFeCoNi-based high-entropy alloys with trace Si additions

Effect of Ni in SiO 2 coating on the oxidation resistance of TiAl alloy at 900 °C

Oxidation behavior of AlCoCrFeNiSi high-entropy alloys at 1100 °C

Effect of Si content on the microstructure and properties of Ti–Si–C composite coatings prepared by reactive plasma spraying

Oxidation behavior of AlCoCrFeNiSi x high entropy alloy bond coatings prepared by atmospheric plasma spray

Effect of Si Content on Deposition and High-Temperature Oxidation of Al-Si Coatings Obtained by Magnetron Sputtering PVD Method

High temperature oxidation behavior of binary Co-10Si alloys

Influences of Cr contents on oxidation behavior of WC-Co-Ni-Cr cemented carbides at 900 °C

Effect of Si addition to improve the performance of type II and type I hot corrosion resistance of aluminide coating

Effect of Si content on the microstructure and properties of CrSi coatings for ATF cladding

High Temperature Oxidation Behavior of MoSi2-CoNiCrAlY Composite Coating Prepared by Plasma Spraying

Effect of WSi2 content on oxidation behavior of MoSi2-20 vol% Al2O3 composites

Effect of Al content in an Al/Si layer on the oxidation behavior of the Mo/Si-Al/Si double-layer coated C/C composites at 1370°C

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

High Temperature Oxidation Resistance and Degradation Mechanism of Al-Si Coatings on Nickel-Based Superalloy at 1000.

Effect of Al Content in an Al/Si Layer on the Oxidation Behavior of the Mo/Si–Al/Si Double-Layer Coated C/C Composites at 1370 °C