Abstract:Tunnel-type (T-type) Na0.44MnO2 (NMO) is a promising cathode material for sodium-ion batteries (SIBs) owing to its high rate performance and cycling stability compared to manganese-based layered oxides. However, the low specific capacity still restricts its practical applications. Herein, a Co-doped T-type NMO is synthesized through a facile solid-state reaction method and utilized as a cathode material for SIBs. A T-type Na0.44Mn0.9925Co0.0075O2 (NMO-3) electrode can deliver a high reversible capacity of 138 mAh g–1 at 0.1C, a superior rate capability (133, 130, 121, 106, and 93 mAh g–1 at 0.5, 1, 2, 5, and 10C, respectively), and excellent cycling stability (85.2% at 10C after 500 cycles). The substitution of Co3+ by Mn3+ leads to the enlargement of small and S-shaped tunnel spaces, which facilitates the insertion/deinsertion of Na+ into/from NMO-3 and greatly enhances its rate capability and cycling stability. Moreover, the reduced energy barriers for Na+ diffusion in small tunnels make the inactive Na+ easier to be deintercalated, which should be responsible for its high specific capacity that exceeds the theoretical capacity of T-type NMO.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c13278?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c13278</a>.XRD patterns and Rietveld refinement plot (Figure S1); XPS patterns of Mn 2p and Co 2p (Figure S2); SEM, TEM, and HRTEM images (Figure S3); CV curves (Figure S4); charge–discharge profile of the initial three cycles (Figure S5); CV curves at different scanning rates (Figure S6); SEM images after 100, 300, and 500 cycles (Figure S7); Nyquist plots before and after cycling (Figure S8); evolution of lattice parameters obtained by in situ XRD (Figure S9); assembly drawing of the in situ XRD cell (Figure S10); formation energies with different Co-substitution contents (Figure S11); structure evolutions and energy barriers (Figure S12); TEM-HAADF and TEM-EDX element mapping images at a fully charged state (Figure 13); electronic conductivities (Figure S14); lattice parameters from Rietveld refinement (Table S1); ICP-OES (Table S2); content of Mn3+ and Mn4+ (Table S3); dissolution degree of Mn after cycling (Table S4); impedance parameters before cycling (Table S5); impedance parameters after cycling (Table S6); comparison of electrochemical properties (Table S7); and potential of redox peaks by CV curves (Table S8) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13278/suppl_file/am0c13278_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Insights into unrevealing the effects of the monovalent cation substituted tunnel-type cathode for high-performance sodium-ion batteries

Structural Insight into the Abnormal Capacity of a Co-Substituted Tunnel-Type Na0.44MnO2 Cathode for Sodium-Ion Batteries

Structural Insight into the Abnormal Capacity of a Co-Substituted Tunnel-Type Na 0.44 MnO 2 Cathode for Sodium-Ion Batteries

An Advanced Medium-Entropy Substituted Tunnel-Type Na0.44MnO2cathode for High-Performance Sodium-Ion Batteries

Effect of sodium content on the electrochemical performance of Li-substituted, manganese-based, sodium-ion layered oxide cathodes.

Engineering sodium-rich manganese oxide with robust tunnel structure for high-performance sodium-ion battery cathode application

Synergetic Anion-Cation Co-doping in Na 0.44 MnO 2 Boosting a High-Stability and Improved-Kinetics Cathode for Sodium Ion Battery

Solid-State Synthesis of Low-Cost and High-Energy-Density Sodium Layered-Tunnel Oxide Cathodes: Dynamic Structural Evolution, Na+/Vacancy Disordering, and Prominent Moisture Stability

Sodium Stoichiometry Tuning of the Biphasic-Nax MnO2 Cathode for High-Performance Sodium-Ion Batteries.

High Performance Sodium-Ion Full Battery Based on One-Dimensional Nanostructures: the Case of Na0.44MnO2 Cathode and MoS2 Anode

Insight into effects of divalent cation substitution stabilizing P2-Type layered cathode materials for sodium-ion batteries

Lattice regulation strategy for constructing high-rate performance Na0.44Mn0.895Ti0.1Mg0.005O2 sodium-ion batteries cathode materials

Complementary Effect of Ti and Ni Incorporation in Improving the Electrochemical Performance of a Layered Sodium Manganese Oxide Cathode for Sodium-Ion Batteries

Ultrafast and Highly Efficient Sodium Ion Storage in Manganese‐Based Tunnel‐Structured Cathode

Mitigation of Jahn–Teller Distortion and Na+/vacancy Ordering in a Distorted Manganese Oxide Cathode Material by Li Substitution

Modulating the Electrochemical Performances of Layered Cathode Materials for Sodium Ion Batteries Through Tuning Coulombic Repulsion Between Negatively Charged TMO2 Slabs

Manipulating Stable Layered P2‐Type Cathode via a Co‐Substitution Strategy for High Performance Sodium Ion Batteries

The influences of sodium sources on the structure evolution and electrochemical performances of layered-tunnel hybrid Na0.6MnO2 cathode

Sodium substitution for partial lithium to significantly enhance the cycling stability of Li2MnO3 cathode material

Boosting Reversibility of Mn‐Based Tunnel‐Structured Cathode Materials for Sodium‐Ion Batteries by Magnesium Substitution

Li-Substituted Layered Spinel Cathode Material for Sodium Ion Batteries