Abstract:Low temperature preparable p-type transparent conductors are indispensable for flexible transparent electronics. The current research interest in p-type transparent conductors is mainly focused on wide-band gap copper-based oxides. However, the performance of these oxides is generally inferior to their n-type counterparts, and their high preparation temperature is unfavorable for flexible electronic applications. CuI is a p-type transparent conductor that can be prepared at low temperatures and possesses properties comparable to n-type transparent conductors. The commonly used method for preparing CuI films is iodination of Cu films. However, CuI films produced by this method have a frosted-glass-like appearance, the electrical properties are difficult to be regulated, thus is not suitable for electronic devices. In this paper, we have successfully developed CuI−Cu 2 O composite films with enhanced surface morphology and electronic properties at room temperature. Cu 2 O inhibits the movement of CuI grain boundaries during the iodination process, resulting in a reduction of CuI grain size and a polycrystalline organization with a smoother surface. Due to the increased concentration of grain boundaries in the films and the charge redistribution between Cu 2 O and CuI, the hole concentration in the films decreases and the hole mobility increases. The conductivity of the films increases and then decreases as the Cu 2 O content rises. For CuI−Cu 2 O films with optimized Cu 2 O composition, the transparency in the visible region is 70-80%, the hole concentration is 6.16×1018 cm -3 , the hole mobility is 25.40 cm 2 V -1 s -1 , and the conductivity is 18.57 S cm -1 . After 6 months of aging, the electrical properties of CuI−Cu 2 O films are more stable than those of pure CuI films. These findings will accelerate the wide application of CuI films in transparent electronics.

Amorphous Transparent Cu(S,I) Thin Films with Very High Hole Conductivity

Highly Conductive p-Type Transparent Conducting Electrode with Sulfur-Doped Copper Iodide

High-Performance p-Type Transparent Conducting CuI−Cu2O Thin Films with Enhanced Hole Mobility, Surface, and Stability

Highly Enhanced P-Type Electrical Conduction in Wide Band Gap Cu1+xAl1−xS2 Polycrystals

Cs‐Doped and Cs‐S Co‐Doped CuI p‐Type Transparent Semiconductors with Enhanced Conductivity

Room-temperature synthesized copper iodide thin film as degenerate p-type transparent conductor with a boosted figure of merit

P-Type Transparent Conductor: Zn-doped CuAlS2

Copper‐alloyed ZnS As a P‐type Transparent Conducting Material

Effect of Hole Effective Mass and Carrier Concentration on the Conductivity of a Transparent P‐type LaCuOS Semiconductor with Good Transmittance in Both Visible and Mid‐Infrared Ranges

1.37×102 S·cm-1 P-Type Conductivity LaCuOS Films with a Very Wide Optical Transparency Window of 400-6000 Nm

Recent Research of Cu-based Transparent Conducting Materials with p-type

A Transparent p-Type Semiconductor Designed via a Polarizability-Enhanced Strongly Correlated Insulator Oxide Matrix

Amorphous P-Type CuNiSnO Thin-Film Transistors Processed at Low Temperatures

A P-type Mid-Infrared Transparent Semiconductor LaSe2 Film with Small Hole Effective Mass and High Carrier Concentration

Electronic Structure of Amorphous Copper Iodide: A p-type Transparent Semiconductor

8‐4: Invited Paper: Transparent Zn Doped‐CuI for High‐Performance P‐channel Thin Film Transistors

Design and discovery of a novel Half-Heusler transparent hole conductor made of all-metallic heavy elements

Epitaxial Bi<sub>2</sub>Sr<sub>2</sub>CuOu<sub> <i>y</i> </sub> thin films as p-type transparent conductors

High-performance P-Channel Transistors with Transparent Zn Doped-Cui

Solution-processed amorphous p-type Cu-Sn-I thin films for transparent Cu-Sn-I/IGZO p–n junctions

A P-type mid-infrared transparent semiconductor LaSe 2 film with small hole effective mass and high carrier concentration