Fabrication And Characterization Of Titanium-Based Lead Dioxide Electrode By Electrochemical Deposition With Ti4o7 Particles
Hua Guo,Zhicheng Xu,Dan Qiao,Liangtian Wang,Hao Xu,Wei Yan
DOI: https://doi.org/10.1002/wer.1339
2021-01-01
Water Environment Research
Abstract:A novelly modified Ti/PbO2 electrode was synthesized with Ti4O7 particles through electrochemical deposition method (marked as PbO2-Ti4O7). The properties of the as-prepared electrodes were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS), hydroxyl radical concentration, accelerated life test, etc. Azophloxine was chosen as the model pollutant for electro-catalytic oxidation to evaluate electrochemical activity of the electrode. The experimental results indicated that Ti4O7 modification could prominently improve the properties of the electrodes, especially, improve the surface morphology, enhance the current response, and reduce the impedance. However, the predominant phases of PbO2 electrodes were unchanged, which were completely pure beta-PbO2. During the electrochemical oxidation process, the PbO2-Ti4O7(1.0) electrode showed the best performance on degradation of AR1 (i.e., the highest removal efficiency and the lowest energy consumption), which could be attributed to its high oxygen evolution potential (OEP) and strong capability of HO center dot generation. Moreover, the accelerated service lifetime of PbO2-Ti4O7(1.0) electrode was 175 hr, 1.65 times longer than that of PbO2 electrode (105.5 hr).Practitioner pointsPbO2/Ti4O7 composite anode was fabricated through electrochemical co-deposition.Four concentration gradients of Ti4O7 particle were tested.PbO2-Ti4O7(1.0) showed optimal electrocatalytic ability due to its high OEP and HO center dot productivity.