Synthesis and Characterization of Titanium Doped Sodium Beta″-Alumina

Xiaoling Wei,Yin Cao,Lei Lu,Hui Yang,Xiaodong Shen

DOI: https://doi.org/10.1016/j.jallcom.2011.03.006

IF: 6.2

2011-01-01

Journal of Alloys and Compounds

Abstract:High dense Na–β″-Al2O3 electrolyte materials have been synthesized by solid state reaction with boehmite, magnesia, sodium carbonate and titania as the starting materials. The effects of TiO2 doping percentage on the properties and microstructures of the prepared samples were investigated by X-ray diffraction (XRD), scan electron microscope (SEM), three point bending and ionic conductivity tests. The results indicated that both the relative densities and the phase purities of the samples could effectively improved after doping with TiO2. The proper doping amount of TiO2 was to form the transient liquid phase during the sintering process, which would reduce the steric effect and accelerate the diffusivity. Moreover, the mechanical performance of the obtained sample increased to the value above 280MPa as the doping amount of TiO2 was larger than 1wt%. As to the electric properties, if the doping amount was less than 1wt%, the grain boundary resistivity reduced as the density increased, so the ionic conductivity of the Na–β″-Al2O3 was enhanced obviously. However, when the doping amount was above 1wt%, the ionic conductivity was deteriorated because of the increased resistivity caused by the broadening grain size.