Abstract:In this work, two isothermal sections of the Co-Ta-Si ternary system at 900 °C and 1100 °C are constructed in the whole composition range via phase equilibrium determination with the help of electron probe microanalysis (EPMA) and X-ray diffraction (XRD) techniques. Firstly, several reported ternary phases G (Co16Ta6Si7), G″ (Co4TaSi3), E (CoTaSi), L (Co3Ta2Si) and V (Co4Ta4Si7) are all re-confirmed again. The G″ phase is found to be a kind of high-temperature compound, which is unstable at less than 1100 °C. Additionally, the L phase with a large composition range (Co32–62Ta26–36Si10–30) crystallizes with a hexagonal crystal structure (space group: P63/mmc, C14), which is the same as that of the binary high-temperature λ1-Co2Ta phase. It can be reasonably speculated that the ternary L phase results from the stabilization toward low-temperature of the binary λ1-Co2Ta through adding Si. Secondly, the binary CoTa2 and SiTa2 phases are found to form a continuous solid solution phase (Co, Si)Ta2 with a body-centered tetragonal structure. Thirdly, the elemental Si shows a large solid solubility for Co-Ta binary compounds while the Ta and Co are hardly dissolved in Co-Si and Ta-Si binary phases, respectively.

Vertical section phase diagrams of La−Fe−B ternary system

Subsolidus Phase-Relations Of The La-Fe-Al Ternary-System

Phase Relations of the (Pr1-Xsmx)(2)fe14b System

Experimental Determination of the Phase Relations of the Sm–Fe–B Ternary System at 973 K

Experimental Investigation On The Phase Equilibria Of The Nb-Ti-Si-B System At 1500 A Degrees C

Experimental Investigation on the Phase Equilibria of the Nb-Ti-Si-B System at 1500 °C

The 600 °C and 450 °C Isothermal Sections of the Zn–Fe–B System

Phase precipitation behavior of rapidly quenched ternary La–Fe–B alloy and the effects of Nd substitution

Phase Equilibria of the Al-Zn-Bi-Fe Quaternary System at 600 A degrees C

Thermodynamic Assessment of La–Fe–Si Systems

Experimental Investigations of the Ho-Fe-B phase diagram at 800 °C using diffusion couples

Phase Equilibria in the Fe-Al-Nb(-B) System at 700 °C

Experimental Investigation and Thermodynamic Calculation of the Phase Equilibria in the Cu-Fe-Ta System

The 600 °C and 700 °C Isothermal Sections of the Zn-Fe-Bi Ternary System

Investigation on the 773 K Isothermal Section of La-Fe-Sn Ternary Systems by X-Ray Powder Diffraction

Phase Diagram of the Nd2Fe14B–Sm2Fe14B Pseudo-Binary System

Experimental Determination of Phase Equilibria in the Fe–Nb–V Ternary System

Phase equilibria in the ternary Al–Zr–La system

Experimental Investigation of Phase Equilibria in the Fe-Nb-Ta System

Phase Relations of Li2O–FeO–B2O3 Ternary System and Electrochemical Properties of LiFeBO3 Compound

Phase Equilibria of the Al–Zn–Bi–Fe Quaternary System at 600 °C