Phase precipitation behavior of rapidly quenched ternary La–Fe–B alloy and the effects of Nd substitution

Z Y Zhang,L Z Zhao,J S Zhang,X C Zhong,W Q Qiu,D L Jiao,Z W Liu
DOI: https://doi.org/10.1088/2053-1591/aa7d85
IF: 2.025
2017-08-02
Materials Research Express
Abstract:To understand the structure and phase precipitation behavior of the ternary La–Fe–B alloy, the effects of wheel speed and heat treatment on the melt spun La2Fe14B alloy were investigated. The results show that the hard magnetic La2Fe14B (2:14:1) phase is difficult to obtain in the ternary alloy. The α-Fe and La phases mainly precipitated as spun ribbons prepared at relatively low wheel speeds, and a more amorphous phase formed at higher wheel speeds. With the annealing temperature increasing from 400 °C to 500 °C and 800 °C, the α-Fe and La phases also gradually precipitated from the amorphous matrix. A liquid La-rich phase and α-Fe phase could coexist in the alloy at high temperature. However, the substitution of Nd for La can greatly enhance the formation of a hard 2:14:1 phase. The effects of Nd substitution on the structure and phase precipitation during annealing for the (La1−x Nd x )2Fe14B (x = 0.1. 0.2, 0.3 and 0.4) alloys have been also investigated. The present results are important for exploring high-performance low-cost La-based Nd–Fe–B magnets.
materials science, multidisciplinary
What problem does this paper attempt to address?