Abstract:This study investigates the change in the acoustic emission (AE) parameters emitted in rubberized concrete under abrasion action at a sub-freezing temperature (−20°C). Seven concrete mixtures were developed with two coarse-to-fine aggregate ratios (C/F) (2.0 and 0.7), various crumb rubber (CR) content (0%, 10%, 20%, and 30%), and different rubber particle sizes [4.5 mm CR and 0.4 mm powder rubber (PR)]. Rotating cutter tests were conducted on three 100 mm cubic samples from each mixture at −20°C and 25°C while monitored via an AE system. AE parameters such as amplitude, number of hits, and signal strength were collected and underwent two parameter-based analyses: b-value and intensity analysis approaches, resulting in three additional parameters: b-value, severity (Sr), and the historic index [H(t)]. Results showed that testing concrete samples under abrasion at cold temperature,−20°C, resulted in a decrease in the emitted number of hits, cumulative signal strength (CSS), Sr, H(t), and an increase in b-values compared to testing at 25°C. Furthermore, incorporating rubber particles was found to decrease the AE signals’ amplitudes significantly at 25°C and slightly at −20°C, which manifested the higher wave attenuation occurrence at ambient temperature compared to cold temperature. AE analysis also showed a decrease in the abrasion resistance for mixtures with higher C/F, higher CR content, and larger rubber particle size. These decreases were more noticeable at 25°C compared to −20°C. Finally, the study developed two damage classification charts to estimate the ranges of abrasion mass loss percentage and wear depth in terms of the intensity analysis parameters: Sr and H(t).

Influence of Mixture Compositions on Impact Resistance and Mechanical Properties of Concrete Cured in Cold Temperature Conditions

Extreme Cold Mechanical Properties of Concrete with Additive-Based Freeze Protection System

Mechanical and Microstructural Properties of Nanoconcretes Exposed to Low-Temperature Curing

Modeling and Mesoscale Simulation of Ice-Strengthened Mechanical Properties of Concrete at Low Temperatures

Experimental investigation on electrical response and mechanical performance of cementitious materials at low temperatures

Investigating the Strength and Microstructure of Cemented Sand–Gravel Mixtures Subjected to Freeze–Thaw Cycles

Experimental studies and numerical analysis of the dynamic mechanical properties of concrete at low temperatures

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

STUDY ON THE MECHANICAL PERFORMANCE AND INFLUENCING FACTORS OF THE CONCRETE AT SUBZERO TEMPERATURE

Mechanics Properties of Concrete at Low Temperature

Effect of Low Temperature on Mechanical Properties of Concrete with Different Strength Grade

Early Age Performance of OPC-GGBFS-Concretes Containing Belite-CSA Cement Cured at Sub-Zero Temperatures

Research on the Mechanical Properties of Concrete under Low Temperatures

Effects of nano-alumina on Portland concrete at low temperatures (5 °C)

Influence of Water Content on Mechanical Strength and Microstructure of Alkali-Activated Fly Ash/GGBFS Mortars Cured at Cold and Polar Regions

Transport Properties and Deicing Salt Resistance of Blended Ultrahigh-Performance Concrete

Influence of high altitude on the strength of aerated concrete

Repeated Impact Response of Normal- and High-Strength Concrete Subjected to Temperatures up to 600 °C

Acoustic Emission Waves Propagation in Rubberized Concrete under Special Monitoring Conditions

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Testing Method and Mechanical Properties of Concrete at Low Temperature