Fabrication of porous β-TCP/58S bioglass scaffolds via top-down DLP printing with high solid loading ceramic-resin slurry

Xiang Li,Hang Zhang,Yifan Shen,Yinze Xiong,Lanlan Dong,Jiangtao Zheng,Shichang Zhao

DOI: https://doi.org/10.1016/j.matchemphys.2021.124587

IF: 4.778

2021-07-01

Materials Chemistry and Physics

Abstract:<p>High solid loading of ceramic slurry limits the wider use of digital light processing (DLP) in the production of porous ceramic scaffolds with advanced functions. The top-down digital light processing (DLP) system is a potential method to achieve ceramic-resin slurry with high solid loading. Porous β-tricalcium phosphate/58S bioglass (β-TCP/BG) scaffolds with high solid loading ceramic slurry were fabricated by the top-down DLP technique in this paper. Photosensitive β-TCP/BG-resin slurries with various solid loadings for DLP were developed and the effects of solid loading on viscosity and curing reactivity were evaluated. The microstructure, mechanical strength, porosity, and shrinkage of the composite scaffolds were then explored. The results show that the maximum viscosity of the β-TCP/BG-resin slurry for top-down DLP technique was 85.92 Pa·s with a solid loading of 60wt%. The cure depth and overgrowth tended to decrease with the solid loading. The curing depth exceeds 100μm at each solid loading after 18000ms irradiation time. The shaping error and sintering shrinkage of the porous structure were estimated, and it was found that the pore size and sintering shrinkage reaching a minimum value for the scaffolds fabricated by the slurry of 60wt%. The compressive strength of the β-TCP/BG scaffolds increased with the solid loading increased, reaching a maximum value of 11.43 ± 0.4 MPa for the solid loading of 60 wt%. β-TCP/BG scaffolds exhibited an alkalescent pH environment and an improved ability of apatite-mineralization formation, meanwhile Ca, P and Si were gradually released from scaffolds. Furthermore, in vitro evaluation of β-TCP/BG scaffolds was carried out to assess the osteogenic capability. The composite scaffolds displayed intensifying biocompatibility and can facilitate osteoblast proliferation, adhesion, and differentiation. The β-TCP/BG composite scaffold fabricated by top-down DLP with high solid loading ceramic slurry could be considered as a promising alternative substitute even for load-bearing bone tissue engineering applications.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The main purpose of this paper is to address the issues encountered in the digital light processing (DLP) printing of high solid content ceramic slurries, particularly in the preparation of β-tricalcium phosphate (β-TCP)/bioactive glass (BG) composite scaffolds. Specifically, the paper attempts to achieve the following objectives:

1. **Develop high solid content β-TCP/BG photosensitive slurries suitable for DLP printing**:
- Investigate β-TCP/BG photosensitive slurries with different solid contents (45wt% to 60wt%) and evaluate their rheological properties and curing behavior.

2. **Explore the impact of solid content on slurry viscosity and curing reactivity**:
- Analyze the viscosity changes of the slurry at different solid contents, finding that the highest printable solid content is 60wt%, with a viscosity of 85.92 Pa·s.

3. **Prepare porous β-TCP/BG scaffolds using top-down DLP technology**:
- Successfully prepare porous β-TCP/BG scaffolds from high solid content ceramic slurries using top-down DLP technology, which exhibit high compressive strength.

4. **Analyze the impact of solid content on scaffold forming error and sintering shrinkage**:
- The study finds that as the solid content increases, the forming error gradually decreases, and the sintering shrinkage also reduces, reaching a minimum at 60wt%.

Through the above research, the paper aims to develop a method for efficiently printing high solid content ceramic slurries, thereby improving the mechanical properties and biocompatibility of porous ceramic scaffolds for eventual application in bone tissue engineering.