Abstract:The Ti-6Al-4V (TC4) alloy wheel hub has exhibited some defects that affect the properties during the vertical centrifugal casting process. Therefore, the analysis of the solidification process would contribute to solving the above-mentioned problems. In this study, an orthogonal experimental design was employed to optimize the process parameters (rotational speed, mold preheating temperature, and pouring temperature) of the vertical centrifugal casting method. The effects of process parameters on the velocity field, temperature field, and total shrinkage porosity during the solidification process were explored, and the microstructure and mechanical properties of the wheel hub prepared by the vertical centrifugal casting method were also investigated. The results showed that the rotational speed mainly induced the change of the velocity field. The pouring temperature and mold preheating temperature affected the temperature field and solidification time. Based on the analysis of the orthogonal experiment, the optimal parameters were confirmed as a rotational speed of 225 rpm, mold preheating temperature of 400 °C, and pouring temperature of 1750 °C, respectively. The simulation results of total shrinkage porosity were in agreement with the experiment results. The wheel hub was composed of nonuniform α and β phases. The lath α phase precipitated from larger β grains with different orientations. Compared with the other samples at different locations, the α phase in the PM sample (middle of the TC4 wheel hub) displayed high peak intensity and uniformly distributed β phase along the radial direction of the wheel hub. Moreover, the PM sample revealed a higher tensile strength of 820 MPa and similar Vickers hardness of 318 HV compared with the other samples at different locations, which were higher than those of rolling and extrusion molding. This experiment design would provide a good reference for the vertical centrifugal casting of the TC4 alloy.

Low pressure casting mould structure of aluminium alloy wheel hub

Mold Local Temperature Control in Low Pressure Die Casting Aluminum Alloy Wheel Hub

Die Structure Optimization of Aluminum Alloy Wheel Low-Pressure Die Casting Based on CAE

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Numerical Study on the Low Pressure Die Casting of AZ91D Wheel Hub

Multi-Objective Optimization of The Low-Pressure Casting of Large-Size Aluminum Alloy Wheels through a Systematic Optimization Idea

A cast spinning process for aluminum alloy wheel hub

Numerical Simulation of Filling Process and Technology Improvement of Low Pressure Die Casting of Aluminum Wheel Hub

Solidification simulation of automobile wheel in low pressure casting

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Effect of Cooling Process on Porosity in the Aluminum Alloy Automotive Wheel During Low-Pressure Die Casting

Research on the squeeze casting process of large wheel hub based on FEM and RSM

Defects Analysis and Improvement for Electricmotorcar Aluminum Alloy Wheel by Gravity Casting

Simulation of Casting Stress of Low-pressure Casting Aluminum Alloy Wheel

Low Pressure Sand Mould Casting Technology for Heavy Aluminum Alloy Casting

Numerical Simulation on Solidification during Vertical Centrifugal Casting Process for TC4 Alloy Wheel Hub with Enhanced Mechanical Properties

Mechanical Properties and Microstructure of A356-T6 Aluminum Alloy Wheel Hub Based on Casting-Spinning Process

The Design of 3D-Printed Lattice-Reinforced Thickness-Varying Shell Molds for Castings.

Study of Mold Filling Simulation on Low Pressure Die Casting for Automobile Wheel Casting

MOLDING AND CONTROLLING OF HIGH STRENGTH A356 ALUMINIUM ALLOY FOR AUTOMOBILE HUB

Effects of Hollow Sand Mold on the Microstructure and Mechanical Properties of a Low Pressure Aluminum Alloy Casting