Abstract:This article investigates the transformation behavior of the glassy phase and crystalline phase in MnO–SiO2–Al2O3–MgO inclusions during heat treatment. The results show that the diffusion of elements in inclusions during heat treatment promotes the crystallization of the glassy phase, the growth of the crystalline phase and the change of crystal type. This study provides the theoretical basis for inclusion plasticization. To clarify the transformation of the glassy and crystalline inclusions in cord steel during heat treatment, four groups of MnO–SiO2–Al2O3 systems with different MgO contents are designed to obtain samples with both glassy and crystalline inclusions by slow‐cooling, and then the samples are isothermal held at 1100 °C for 120 min. The results of X‐ray diffraction and scanning electron microscope and energy dispersive spectrometer indicate that after isothermal holding, the MgMnSiO4 crystalline phase transforms into MgAl2O4 and MnSiO3 phases in 5 wt% MgO system, while partial MgMnSiO4 phase transforms into MgSiO3 phase in 10 wt% MgO system. Besides, the MgMnSiO4 crystalline phase transforms into MgSiO3 and Mg2SiO4 phases in 15 wt% MgO system, while the Mg2SiO4 crystalline phase partially transforms into MgSiO3 phase in 20 wt% MgO system. Combined with the calculation results of FactSage 8.1, it shows that the higher the MgO content in the system, the stronger the crystallization ability and the easier the formation of the crystalline phase. During the isothermal holding process, the elements in inclusions continuously diffuse and migrate, so that the glassy phase transforms into crystalline phase, while the crystalline phase grows further and the internal glassy phase disappear, accompanied by the transformation of the crystal type.

Evolution of MnO–SiO2–Al2O3–MgO inclusions during heat treatment at 1100 °C

EXPERIMENTAL STUDY ON THE PHASE RELATIONS OF THE SYSTEM Mg2SiO4-MgAl2O4 AT HIGH PRESSURE AND HIGH TEMPERATURE

Study on Transformation of Glassy and Crystalline Inclusions in Cord Steel during Heat Treatment at 1100 °C

Effect of Cooling Conditions on the Size and Morphology Evolution of MgAl2O4 Inclusions in Al‐Deoxidized Steel Coupling with Mg Treatment

Evolution of Interfacial Features of MnO-SiO2 Type Inclusions/Steel Matrix during Isothermal Heating at Low Temperatures

Effect of trace Si on MgO·Al2O3 inclusion in ultra-low-carbon steel

Effect of Mg Treatment on the Evolution of Inclusions in M50 Aerospace Bearing Steel Under Different S/O Ratio Conditions

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Characteristics and Transformation Mechanism of Nonmetallic Inclusions in 304 Stainless Steel during Heat Treatment at 1250 °C

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9

Development of inclusions in 3104 alloy melt during heating and holding treatments

Mg and Al mixed effects on thermal properties in aluminosilicate glasses

The phase composition and microstructural evolution of a novel MgO-C-Al-Si refractory used in bottom-blowing elements at high temperatures in flowing nitrogen

Microstructure and mechanical properties of MgO–Al2O3–SiO2–TiO2 glass–ceramics

Evolution of Inclusions and Associated Microstructure in Ti–Mg Oxide Metallurgy Steel

The Effect of Niobium on the Changing Behavior of Non-Metallic Inclusions in Solid Alloys Deoxidized with Mn and Si during Heat Treatment at 1473 K

Effect of melt holding on morphological evolution and sedimentation behavior of iron-rich intermetallic phases in Al—Si—Fe—Mn—Mg alloy

Heat treatment Effect of Mg-5Sn-3Zn-1Mn Alloy with different Silicon addition

Mechanism of grain refinement and growth for the continuous alumina fibers by MgO addition

Research on Homogenization Treatment of Mg-8wt.% Sn-1.5 Wt.% Al Alloy

Heat Treatment-Induced Microstructure and Property Evolution of Mg/Al Intermetallic Compound Coatings Prepared by Al Electrodeposition on Mg Alloy from Molten Salt Electrolytes