A new way to analyze constitutive analysis and its relation to the microstructure of a Mg-Gd-Y-Zn alloy

Abdul Malik,Tahir Mehmood Bhatti,Syed Zohaib Hassan Naqvi,Sehreish Abrar,Faisal Nazeer,Abdullah G. Al-Sehemi

DOI: https://doi.org/10.1016/j.jallcom.2024.173456

IF: 6.2

2024-01-10

Journal of Alloys and Compounds

Abstract:It is the first time that we have systematically proved that the activation energy ( Q -value) is the main parameter that controls the dynamic recrystallization during hot deformation, and the reliability of the constitutive analysis is entirely dependent on the Q -value. To this end, the hot deformation behavior of a Mg-Gd-Y-Zn alloy was investigated at the temperatures of range 573 K -723 K under strain rates of range 0.0001–1 s −1 . Subsequently, the Q -value ∼ 331.24 kJ mol −1 was achieved. By considering the two different approaches of eliminating the temperatures and then eliminating the strain rates, the lowest Q-values ∼ 259.75 kJ mol −1 and ∼ 295.80 kJ mol −1 were achieved, respectively. Based on the lowest Q -values, the deduced parameters of temperatures range of 623 K -723 K and strain rates range of 0.0001–0.01 s −1 were evaluated. Interestingly, the numerical simulation exhibited a further lower Q -value ∼ 237.17 kJ mol −1 . The difference in the Q -values revealed that the large strain hardenability is due to the high Q -value, while the low strain hardenability is due to the low Q -value. The deduced parameters were also well-matched with the processing maps and the EBSD analysis. Last but not least, the deduced parameters displayed a high accuracy in predicting the flow stresses. Thus, the new approach is of great significance in analyzing the accurate calculation of Q -value, the correctness of constitutive analysis, and evaluating stress-strain behavior.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering