Covalently Anchoring an Ultrathin Conformal SiOx Coating on Polyolefin Separator for Enhanced Lithium Metal Battery Performance
Yulin Zhang,Jianhao Lu,Zhaoqing Jin,Xintai Xie,Lei Wei,Pengfei Li,Yao Zhao,Jiachang Zhao,Caihong Xu,Weikun Wang,Zongbo Zhang
DOI: https://doi.org/10.1002/adfm.202417160
IF: 19
2024-11-13
Advanced Functional Materials
Abstract:This work presents a scalable, binder‐free precursor solution approach to fabricate an ultrathin (≈20 nm), covalently bonded SiOx coating on a polyethylene (PE) separator (SiOx‐co‐PE). The SiOx‐co‐PE separator demonstrates remarkably promoted thermal stability, mechanical strength, and electrolyte wettability without increasing thickness, leading to superior dendrite resistance and cycling stability in lithium metal batteries. Surface modification of separators with inorganic oxide ceramics such as SiOx, Al2O3, and TiO2 has emerged as a promising strategy to suppress lithium dendrite growth in lithium metal batteries, thereby enhancing safety and extending battery life. However, the binder‐dependent nature of these modifications often leads to increased separator thickness and a heightened risk of detachment during lithium plating, ultimately compromising both battery performance and energy density. In this study, a conformal, ultrathin (≈20 nm) SiOx coating with strong covalent bonding is grown on a porous separator through a liquid polymer‐derived method. Compared to the pristine polyethylene (PE) separators, this SiOx‐co‐PE separator exhibits significantly improved electrolyte wettability, mechanical strength, and thermal stability without any increase in thickness, leading to vastly enhanced cycling stability and dendrite resistance in cells with Li metal anodes. In a practical demonstration, a 402.9 Wh·kg−1 Li‐S pouch cell, with a high sulfur loading of 9 mg cm−2 and a low E/S ratio of 3.3 μL mg−1, is assembled with the SiOx‐co‐PE separator, achieving stable cycling over 70 cycles at 25 °C.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology