A Polar and Ordered-Channel Composite Separator Enables Antidendrite and Long-Cycle Lithium Metal Batteries
Zhen Wu,Zhipeng Cai,Bin Fang,Meinan Liu,Huaping Wu,Aiping Liu,Fangmin Ye
DOI: https://doi.org/10.1021/acsami.1c02951
2021-05-27
Abstract:Lithium (Li) metal as an anode replacing the traditional graphite could largely enhance the specific energy density of Li batteries. However, the repeated formation of solid electrolyte interfaces on the surface of Li metal upon plating/stripping leads to a low Coulombic efficiency, and the growth of Li dendrites upon cycling probably causes the short circuit or even explosion of the batteries, both of which block the commercial application of Li metal in lithium metal batteries (LMBs). Herein, we report an antidendrite composite separator fabricated by a two-step method, which features the ordered pore channels and the polar groups in the channels. This novel composite separator has a good wettability to the electrolyte, high mechanical properties, and high ionic conductivity. Expectedly, the assembled batteries based on our novel composite separator show many impressive performances. In Li–Li cells, the cycling life up to 1600 h at an areal current density of 2 mA/cm<sup>2</sup> can be realized; in Li–Cu cells, the cycling life of more than 1000 h with a high Coulombic efficiency of 99.9% at 1 mA/cm<sup>2</sup> can be achieved. More interestingly, the Li/LiFePO<sub>4</sub> full batteries constructed by the novel composite separators show a high discharge capacity of 140 mAh/g and weak capacity decays even after 360 cycles. The novel design of the separator with ordered channels and polar groups presents an effective route for developing the next-generation LMBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02951?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02951</a>.SEM images, EDS elemental mapping images, BET patterns, optical images of the fracture process, XRD patterns, TGA curves, XPS pattern, ionic conductivity, and contact angles for the samples; voltage profiles of the Li–Li cell and cycling performance for the Li–Cu cell; FTIR spectra and Nyquist plots for the cycled Li–Li cells; CV curves and capacity–voltage profile for Li/LFP batteries (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02951/suppl_file/am1c02951_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology