A separator coated with commercial LiFePO4 and conductive carbon for Li-S battery of good cycling performance
Shuang Xia,Zhichao Chen,Lixuan Yuan,Jie Song,Qi Zhou,Xinhai Yuan,Lili Liu,Lijun Fu,Yuhui Chen,Yuping Wu,Xia Shuang
DOI: https://doi.org/10.1039/d3ta03527a
IF: 11.9
2023-08-30
Journal of Materials Chemistry A
Abstract:Li-S batteries can meet the demand of market development in terms of high energy density, but the notorious 'shuttle effect' and lithium dendrites pose a great threat to their cycling and safety performance, which greatly hinders their commercialization process. Under high sulfur loadings and high current densities, unsatisfactory cycling performances are also headache issues. Here, modified separators (SPLFPPD) with LiFePO4 (LFP) and Super P coating on the original separators (DKJ-14) are prepared to solve the above problems. The SPLFPPD has the advantages of the physical barrier to the polysulfides and promoting the catalytic conversion of polysulfides (S2- and sulfides). Besides, the SPLFPPD can enable the uniform deposition of lithium ions, increase ionic conductivities, and fully utilize active S substances. The capacity attenuation of the assembled Li-S batteries with the SPLFPPD is 0.062% per cycle at 1 C after 800 cycles, and 0.045% per cycle at 5 C after 1000 cycles. The specific capacity can be stable to above 500 mAh g-1 after 400 cycles at 0.2 C with high S loading of 4.0 mg cm-2. After 100 cycles, no signs of corrosion or lithium dendrites were observed. The work provides a feasible way of commercial separators for high-performance Li-S batteries.
materials science, multidisciplinary,chemistry, physical,energy & fuels