Abstract:The core-shell structural Fe 3 O 4 @MBT-LDH was synthesized via the ion exchange method, with MBT (2-mercaptobenzothiazole) inhibitor ions intercalated lamellar ZnAlCe-LDH attaching closely to the Fe 3 O 4 microspheres surface. The morphology, composition, structure, and magnetic properties of the composite were measured by transmission electron microscope, X-ray diffraction, Fourier transform infrared spectra, and vibrating sample magnetometer. The release behavior of MBT ions and corrosion inhibition performance of the Fe 3 O 4 @MBT-LDH under "no MF" (without an external magnetic field) and "MF ON" modes (under an external magnetic field) were measured by UV–vis spectroscopy, electrochemical tests, scanning electron microscopy, and X-ray photoelectron spectrometer (XPS). Calcinating the composite after the release test and redispersing the sintered products in MBT ions-containing solution, the composite was reestablished. Results showed that the Fe 3 O 4 @MBT-LDH possessed moderate MBT loadings amount (12.0%) and presented strong superparamagnetic properties with saturation magnetization ( M s) of 27.6 emu⋅g −1 . The release behavior of the MBT − from the composite was sustainable and could be further slowed down by using an external magnetic field with changing the release mechanism. The release curve reached equilibrium with a longer time of 48 h and a lower release amount of 57.0% under MF ON mode than that of no MF mode with a time of 7 h and a release amount of 74.7%. The Fe 3 O 4 @MBT-LDH owned a good and long-term protection performance for Q235 carbon steel with maximum corrosion inhibition efficiency ( η e ) of up to 93.30%. As a promising controlled-release inhibitor, it could be recycled and regenerated by simple treatment, still having high η e higher than 80% and excellent magnetic properties with M s of 21.47 emu⋅g −1 after five cycles. The corrosion mechanism for carbon steel was further analyzed by quantum chemical calculations and molecular dynamics simulation.

Facile synthesis of novel hierarchical core@shell structural magnetic nanovehicle Fe3O4@ZnAlCe-MoO4-LDHs for carbon steel protection

Constructing Carbon-Coated Fe3O4 Hierarchical Microstructures with a Porous Structure and Their Excellent Cr(VI) Ion Removal Properties

Preparation of magnetic core-shell Fe 3 O 4 @MBT-LDH composite and its application as an effective inhibitor for carbon steel

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Anticorrosion Coating with Heterogeneous Assembly of Nanofillers Modulated by a Magnetic Field.

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Composite Nanocontainers Synthesized by In-Situ Growth of Metal Organic Frameworks on Layered Double Hydroxides Having Both Passive and Active Protecting Capabilities

Preparation and inhibition behavior of Fe3O4/MBT nanocomposite inhibitor for mild steel in NaCl solution

Synthesis of Magnetic Core–shell Iron Nanochains for Potential Applications in Cr(VI) Ion Pollution Treatment

MoO42−-LDH films for active protection of steel substrates by Electrodeposition–Hydrothermal method

Developing epoxy-based anti-corrosion functional nanocomposite coating with CaFe-Tolyl-triazole layered double hydroxide@g-C3N4 as nanofillers on Q235 steel substrate against NaCl corrosive environment

Intelligent anti-corrosion coating with multiple protections using active nanocontainers of Zn Al LDH equipped with ZIF-8 encapsulated environment-friendly corrosion inhibitors

Construction of Bta-Inbuilt Zif-8 Coated with Molybdate-Intercalated Znal-Ldh As Core-Shell Structured Nanocontainers Toward Ph-Responsive Smart Corrosion Protection of Waterborne Epoxy Coating

Multifunctional liquid-like magnetic nanofluids mediated coating with anticorrosion and self-healing performance

Morphology and Anti-Corrosive Performance of Cr(III) Passivated Zn-Fe Alloy Coating on NdFeB Substrate

Constructing Superhydrophobic WO3@TiO2 Nanoflake Surface Beyond Amorphous Alloy Against Electrochemical Corrosion on Iron Steel

Kinetically-controlled formation of Fe2O3 nanoshells and its potential in Lithium-ion batteries

Double-Ligand Strategy to Construct an Inhibitor-Loaded Zn-MOF and Its Corrosion Protection Ability for Aluminum Alloy 2A12

Ni-Co hydrotalcite modified diatom to achieve corrosion inhibition and Cl − adsorption for long-term corrosion protection of steel

Outstanding anti-corrosion performance in Nd–Fe–B permanent magnets by constructing a hydrophobic triplex surface coating

Designing a self-healable nano-structured thin film based on sustainable cerium-loaded ZIF8-MOF particles