Construction of Bta-Inbuilt Zif-8 Coated with Molybdate-Intercalated Znal-Ldh As Core-Shell Structured Nanocontainers Toward Ph-Responsive Smart Corrosion Protection of Waterborne Epoxy Coating

Chenyang Zhao,Yi Huang,Yue Li,Chen Wang,Wenlin Yuan,Di Cheng,Tao Shen,Ji Zhang,Jie Liu,Chao Yang,Chunchun Wu,Qianhong Shen,Hui Yang

DOI: https://doi.org/10.1016/j.porgcoat.2024.108623

IF: 6.6

2024-01-01

Progress in Organic Coatings

Abstract:Nanocontainers encapsulating corrosion inhibitors are commonly incorporated into organic coatings to enable self-healing effects, thereby ensuring long-term anticorrosion performance. In this study, a novel dual corrosion inhibitor-loaded self-healing nanocontainer with core-shell structure was proposed for fabricating composite waterborne epoxy coatings with both active and passive corrosion prevention properties.The nanocontainer, named BTA-ZIF-8@LDH-Mo, was synthesized through the in-situ growth of molybdate-intercalated ZnAl layered double hydroxide (LDH-Mo) on the surface of 1H-benzotriazole-inbuilt zeolitic imidazolate framework (BTA-ZIF-8). Potentiodynamic polarization results showed that the Icorr of bare Q235 carbon steel immersed in a 3.5 wt% NaCl solution decreased from 4.658 × 10−6 A/cm2 to 1.274 × 10−6 A/cm2 after introducing BTA-ZIF-8@LDH-Mo nanocontainers, resulting in a superior corrosion inhibition efficiency of 72.65 %. Electrochemical impedance spectroscopy further demonstrated that the |Z|f=0.01Hz of epoxy coating doped with BTA-ZIF-8@LDH-Mo reached 4.24 × 109 Ω·cm2 after 42 d of immersion in 3.5 wt% NaCl solution, approximately 30 times higher than that of pure EP coating. Moreover, investigations on artificially scratched coatings indicated that the incorporation of BTA-ZIF-8@LDH-Mo nanocontainers effectively mitigated the corrosion process by forming an inhibiting layer on the metal substrate that impeded the corrosion process. The dual corrosion inhibitor strategy relies on the synergistic action of BTA pre-loaded in ZIF-8 nanoparticles and molybdate (MoO42-) intercalated in LDH interlayers for active corrosion protection. Additionally, the nanocontainers enhance passive protection by elongating the diffusion paths of corrosive media and trapping chloride ions. This nanocontainer design offers a facile strategy for fabricating a smart coating with the excellent anticorrosion properties.